Formation of porous carbon materials with in situ generated NaF nanotemplate.

نویسندگان

  • Chih-Hao Huang
  • Yu-Hsu Chang
  • Hsiao-Wan Wang
  • Soofin Cheng
  • Chi-Young Lee
  • Hsin-Tien Chiu
چکیده

Porous carbon materials with pore sizes from 3 to 200 nm were synthesized by reacting hexafluorobenzene with Na liquid at 623 K. NaF crystals, a byproduct formed in the reaction, acted as nanotemplate to assist the pore formation. By employing hexafluorobenzene to react with Na incorporated within the channels (diameter 200 nm) of anodized aluminum oxide (AAO) membranes at 323-623 K, the carbon material can be fabricated into aligned porous nanotube arrays (ca. 250 nm in diameter, ca. 20 nm in wall thickness, ca. 0.06 mm in length, and ca. 3-90 nm in pore diameter). These materials were characterized by X-ray diffraction, scanning and transmission electron microscopy, X-ray energy dispersive spectroscopy, electron diffraction, thermal gravimetric analysis, and nitrogen physical adsorption experiments.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

THE EFFECT OF CRYOLITE NA3ALF6 AND SODIUM FLUORIDE NAF ON THE CORROSION AND WETTING BY MOLTEN AL-SI ALLOY OF ANDALUSITE BASED REFRACTORIES

In order to improve the corrosion resistance of aluminosilicate refractories by molten aluminum, alkaline fluoride NaF and cryolite Na3AlF6 powders were studied. Both physical and chemical properties are known to influence wetting and corrosion behavior. This paper devoted to determine the influence of alkaline fluoride and cryolite added to andalusite based castable on the reaction with a...

متن کامل

Formation of Foam-like Microstructural Carbon by Carbonization of Porous Coordination Polymers via Ligand-assisted Foaming Process

Porous carbon with a foam-like microstructure has been synthesized by direct carbonization of porous coordination polymer (PCP). In situ generation of foaming agents by chemical reactions of ligands in PCP during carbonization provides a simple way to create lightweight carbon with a foam-like microstructure. Among several substituents, the nitro group has been proved to be the key to obtain th...

متن کامل

Nitrogen-doped porous carbon materials generated via conjugated microporous polymer precursors for CO2 capture and energy storage

Heteroatom doping and well-tuned porosity are regarded as two important factors of porous carbon materials (PCMs) for various applications. However, it is still difficult to tune a single variable while retaining the other factors unchanged, which restricts rational and systematic research on PCMs. In this work, in situ nitrogen-doped porous carbon material (NPCM-1) and its non-doped analogue P...

متن کامل

The effect of nano transition metals on microstructure and phase evolution of low carbon MgO-C refractories

In the present study, the effect of Iron Nitrate as catalytic precursor to in situ formation of nano-Fe particles in phenolic resin and microstructural evolution of MgO-C refractories has been investigated. Therefore, various samples according to matrix section formulation of low carbon MgO-C refractories (LCMCR’s) with 0 and 6 wt% (Fe/Phenolic resin) were prepared and phase and microstructure ...

متن کامل

Synthesis of WC-8Co cermet powder in WO3-Co3O4-C system by in situ carbothermic solid reduction method under hydrogen atmosphere: (phase, microstructural and thermodynamic analysis)

WC-Co cermets are among the advanced engineering materials that are considered for their special properties such as abrasion resistance and high hardness. The aim of this study was to determine the optimal amount of carbon in raw materials and industrial production of WC-8Co cermet powder from metal oxides WO3, Co3O4 and activated carbon by solid carbothermic reduction method in situ and under ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • The journal of physical chemistry. B

دوره 110 24  شماره 

صفحات  -

تاریخ انتشار 2006