Effect of Wood Flour Content on the Hardness and Water Uptake of Thermoplastic Polymer Composites
نویسنده
چکیده
Polypropylene/wood flour composites were melting compounded in an internal mixer at 190°C and 60 rpm rotor speed and then samples were fabricated by injection molding. Effects wood flour content on the physical properties of composites was investigated. For this purpose, hardness, water absorption and thickness swelling of samples was determined at different levels of wood flour content. The results indicated that the hardness of composites increased with increasing of wood flour content. Also, with increasing of wood flour loading the water absorption and thickness swelling of wood plastic composites increased. It seems that the physical properties of the polypropylene/wood flour composites will be improved by increasing addition of coupling agent.
منابع مشابه
Dynamic Mechanical Analysis of Compatibilizer Effect on the Mechanical Properties of Wood Flour-High-Density Polyethylene Composites
In this study, effect of MAPE (maleic anhydride polyethylene) as the compatibilizer on the mechanical properties of wood-flour polyethylene composites has been investigated by using Dynamic Mechanical Analysis (DMA). Composites were made at 25% and 50% by weight fiber contents and 1% and 2% compatibilizer respectively. Controls were also made at the same fiber contents without the compatibilize...
متن کاملEvaluation on the Effect of Wood Flour and Coupling Agent Content on the Hygroscopic Thickness Swelling Rate of Polypropylene Composites
The effect of wood flour and coupling agent content on the hygroscopic thickness swelling rate of polypropylene composites was investigated in this study. To meet this objective, the wood flour was compounded with polypropylene and coupling agent in an internal mixer; then the samples were fabricated by injection molding. The concentration was varied from 40 to 60% for wood flour and from 0 to ...
متن کاملPolystyrene/wood composites and hydrophobic wood coatings from water-based hydrophilic-hydrophobic block copolymers
D. J. Gardner Department of Forest Management and Advanced Engineered Wood Composites Center, University of Maine, Orono, ME 04469, USA Abstract The combination of synthetic thermoplastic polymers and wood is normally problematic because wood surfaces are hydrophilic while typical thermoplastic polymers are hydrophobic. A possible solution is to use block copolymer coupling agents. In this work...
متن کاملA novel method for manufacturing of wood flour/PP composites with better fire retardancy and mechanical properties
This study was conducted to investigate the effects of applying methods andamount of ammonium polyphosphate (0, 2 and 4 wt%) on fire retardancy andmechanical properties of wood flour/polypropylene composites. The resultsshowed that addition of fire retardant improved the mechanical properties such astensile and flexural strengths and fire retardancy of composites. But by increasingof fire retar...
متن کاملThermoplastic starch/wood composites: interfacial interactions and functional properties.
Thermoplastic starch (TPS)/wood composites were prepared from starch plasticized with 36 wt% glycerol. The components were homogenized by dry-blending, extruded and injection molded to tensile bars. Tensile properties, structure, deformation, water adsorption and shrinkage were determined as a function of wood content, which changed between 0 and 40 vol% in 7 steps. The modification of TPS with...
متن کامل