Double-perovskite magnetic La2NiMnO6 nanoparticles for adsorption of bovine serum albumin applications
نویسندگان
چکیده
Double-perovskite La2NiMnO6 (LNMO) nanoparticles were synthesized by co-precipitation process, and the adsorption of bovine serum albumin (BSA) protein on these nanoparticles was carried out. The powder samples were annealed at 750, 850, 950, and 1,050°C, respectively. X-ray diffraction (XRD) results reveal that there are double perovskites and exhibit mixed orientations, without any impurity phases. Transmission electron microscopy results as well as the XRD estimate results show that the crystalline size is about 34 to 40 nm. The adsorption of BSA on the magnetic nanoparticles was analyzed using a UV spectrophotometer at room temperature. The results show that the as-prepared LNMO nanoparticles display a good adsorbing ability for BSA, and the nanoparticle sintered at 850°C has the highest value of 219.6 mg/g, which is much higher than others.
منابع مشابه
Application of Magnetic Polymer Particles Modified with β–Cyclodextrin for Adsorption of Bovine Serum Albumin
Magnetic polymer particles which were modified by vinyl groups and subjected topolymerization by vinyl β-Cyclodextrin derivative, has been used as adsorbent for sorption andrelease of bovine serum albumin and the equilibrium and kinetics of the adsorption process werestudied. The absorbability and releasing of this protein through the new polymer has beenmeasured by ultraviolet-visible spectros...
متن کاملExploiting BSA to Inhibit the Fibrous Aggregation of Magnetic Nanoparticles under an Alternating Magnetic Field
The alternating magnetic field was discovered to be capable of inducing the fibrous aggregation of magnetic nanoparticles. However, this anisotropic aggregation may be unfavorable for practical applications. Here, we reported that the adsorption of BSA (bovine serum albumin) on the surfaces of magnetic nanoparticles can effectively make the fibrous aggregation of γ-Fe2O3 nanoparticles turn into...
متن کاملCoating of Iron Oxide Nanoparticles with Human and Bovine Serum Albumins: A Thermodynamic Approach
In this research, the Magnetite nanoparticles (Fe304) were prepared by coprecipitation of Fe3+ andFE solution in alkaline medium. Two kinds of surfactants, cetyl tri methyl ammonium bromide(CTAB) and cetyl pyridinum chloride (CPC) were used in the synthesis. Fe304 Nanoparticles werecoated with human serum albumin (HSA) and bovine serum albumin (BSA). Characteristics ofcoated magnetic nanopartic...
متن کاملThe synthesis and characterization of monodispersed chitosan-coated Fe3O4 nanoparticles via a facile one-step solvothermal process for adsorption of bovine serum albumin
Preparation of magnetic nanoparticles coated with chitosan (CS-coated Fe3O4 NPs) in one step by the solvothermal method in the presence of different amounts of added chitosan is reported here. The magnetic property of the obtained magnetic composite nanoparticles was confirmed by X-ray diffraction (XRD) and magnetic measurements (VSM). Scanning electron microscopy (SEM) and transmission electro...
متن کاملRapid and selective separation for mixed proteins with thiol functionalized magnetic nanoparticles
Thiol group functionalized silica-coated magnetic nanoparticles (Si-MNPs@SH) were synthesized for rapid and selective magnetic field-based separation of mixed proteins. The highest adsorption efficiencies of binary proteins, bovine serum albumin (BSA; 66 kDa; pI = 4.65) and lysozyme (LYZ; 14.3 kDa; pI = 11) were shown at the pH values corresponding to their own pI in the single-component protei...
متن کامل