Evaluation of Bonding Shear Performance of Ultra-High-Performance Concrete with Increase in Delay in Formation of Cold Joints
نویسندگان
چکیده
This study set out to derive the optimal conditions for ensuring the monolithicity of ultra-high-performance concrete (UHPC). Direct shear tests were performed to examine the influence on the bonding shear performance. The experimental variables included tamping and delay, which were set to 0, 15, 30, and 60 min. SEM and XRD analyses of the microstructure and composition were performed. The direct shear tests showed that the bonding shear strength was enhanced by the addition of tamping. For the normal-strength concrete (NSC), it is thought that a monolithicity of around 95% can be attained with a cold joint formation delay up to 60 min. In contrast, while the normalized bonding shear strength reduction of UHPC with a delay of 15 min was the lowest at around 8%, a dramatic degradation in the bonding shear performance was observed after 15 min. XRD analyses of the middle and surface sections revealed the composition of the thin film formed at the surface of the UHPC and, as a result, the main component appeared to be SiO₂, which is believed to be a result of the rising of the SiO₂-based filler, used as an admixture in this study, towards the surface, due to its low specific gravity.
منابع مشابه
The effect of bonding temperature on the characteristics of TLP bonded joints in AISI 2205/BNi-3/AISI 2205 assembly
In the present study, the transient liquid phase bonding of AISI 2205 dual phase stainless steel with amorphous BNi-3 interlayer was carried out. Based on the initial experimental and analytical studies, the parameters of temperature and bonding time were determined. In order to investigate the effect of bonding temperature on the microstructural changes of the joint, bonding was performed in t...
متن کاملEffect of Reinforcement Type on the Tension Stiffening Model of Ultra-High Performance Concrete (UHPC)
Ultra-high performance concrete (UHPC) is a developing concrete and today is increasing to interest using it in structures due to its advantages such as high-compressive strength, modulus of elasticity, highly durability and low-permeability. Therefore, it is necessary to provide models for prediction of nonlinear behavior of this material. This study is aimed to investigate the tension-stiffen...
متن کاملThe effect of bonding temperature on the characteristics of TLP bonded joints in AISI 2205/BNi-3/AISI 2205 assembly
In the present study, the transient liquid phase bonding of AISI 2205 dual phase stainless steel with amorphous BNi-3 interlayer was carried out. Based on the initial experimental and analytical studies, the parameters of temperature and bonding time were determined. In order to investigate the effect of bonding temperature on the microstructural changes of the joint, bonding was performed in t...
متن کاملExperimental Study on TGA, XRD and SEM Analysis of Concrete with Ultra-fine Slag (TECHNICAL NOTE)
The performances of cementitious materials as well as the efficiency of construction are adversely affected at high temperatures. Previous studies have already demonstrated that ultra-fine (alccofine) material accelerates the hydration of cement particles and subsequently improves the mechanical and durability properties of the concrete at normal temperature. Moreover, at higher temperatures th...
متن کاملMicrostructure and mechanical properties evaluation of diffusion bonded joints of titanium to AISI 304 austenitic stainless steel
In this study, diffusion bonding between titanium and AISI 304 austenitic stainless steel by Ag interlayer was investigated. In order to carry out this research, samples prepared after surface preparation were placed inside the fixture and placed at the temperatures of 750,800 and 850 °C in the 30,60 and 90 min in the furnace under argon protective gas. The phase transformation and microstructu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره 9 شماره
صفحات -
تاریخ انتشار 2016