Effect of Nano-TiC Dispersed Particles and Electro-Codeposition Parameters on Morphology and Structure of Hybrid Ni/TiC Nanocomposite Layers

نویسندگان

  • Lidia Benea
  • Jean-Pierre Celis
چکیده

This research work describes the effect of dispersed titanium carbide (TiC) nanoparticles into nickel plating bath on Ni/TiC nanostructured composite layers obtained by electro-codeposition. The surface morphology of Ni/TiC nanostructured composite layers was characterized by scanning electron microscopy (SEM). The composition of coatings and the incorporation percentage of TiC nanoparticles into Ni matrix were studied and estimated by using energy dispersive X-ray analysis (EDX). X-ray diffractometer (XRD) has been applied in order to investigate the phase structure as well as the corresponding relative texture coefficients of the composite layers. The results show that the concentration of nano-TiC particles added in the nickel electrolyte affects the inclusion percentage of TiC into Ni/TiC nano strucured layers, as well as the corresponding morphology, relative texture coefficients and thickness indicating an increasing tendency with the increasing concentration of nano-TiC concentration. By increasing the amount of TiC nanoparticles in the electrolyte, their incorporation into nickel matrix also increases. The hybrid Ni/nano-TiC composite layers obtained revealed a higher roughness and higher hardness; therefore, these layers are promising superhydrophobic surfaces for special application and could be more resistant to wear than the pure Ni layers.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

بررسی سختی و مقاومت به خوردگی پوشش های کامپوزیتی Ni-Co/SiC تقویت شده با میکرو و نانو ذرات SiC

Composite and nanocomposite Ni-Co/SiC coatings were synthesized by electro-codeposition of micro and nano-sized SiC particles with average diameter of 10m and 20nm using horizontal electrodes. Surface morphology, chemical composition, phase composition, hardness and corrosion resistance of the deposited coatings were studied using SEM observations and EDX, XRD, microhardness and polarization ...

متن کامل

Fabrication of TiC particulate reinforced Ni-50Fe super alloy matrix composite powder by mechanical alloying

Mechanical alloying is a powder metallurgy processing technique involving cold welding, fracturing, and rewelding of powder particles in a high-energy ball mill. In this work, NiFe-TiC composite powders were prepared by mechanical alloying process using planetary high-energy ball mill. The effect of TiC addition by weight percent on the NiFe solid solution formation, grain size, lattice paramet...

متن کامل

Effect of Ni content on the reaction behaviors and microstructure of TiB2-TiC/Ni cermets synthesized by MASHS

In this paper TiB2-TiC/Ni cermet with various Ni (20, 40 and 60 wt %) content were synthesized by mechanically activated self-propagating synthesis (MASHS) and effect of the addition of Ni on synthesis parameters and microstructure of synthesized samples were investigated. First raw materials (B4C, Ti and Ni) milled in Ar atmosphere. Then milling powders analyzed by XRD. In next step powders sy...

متن کامل

Nano Dispersed Metal-Ceramic Composite Materials of the Ni-SiO2 system

In the organic field effect transistors (OFETs) generation, the silicon gate oxide is 1-2 nm thick. A shrinking of this thickness down to less than 1 nm for the next generation will led to a couple of orders of magnitude increase in tunnelling as well as leakage currents. NiO-SiO2 can be used in a variety of devices, such as in circuit boards and detectors, including sensors, due to its porous ...

متن کامل

Production of Dispersed Ceramic Nano-Particles in Al Alloy Using Friction Stir Processing

In this research, surface composite layers containing nano sized TiB2, Al2O3-TiB2, ZrO2 and CNT particles have been fabricated on Aluminum alloy substrates by friction stir processing. The effects of different processing variables such as number of passes and strengthening particle distribution, hardness, and wear properties of surface nano...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 9  شماره 

صفحات  -

تاریخ انتشار 2016