Luminescence Properties of ZnO Nanostructures and Their Implementation as White Light Emitting Diodes (LEDs)

In the past decade the global research interest in wide band gap semiconductors has been focused on zinc oxide (ZnO) due to its excellent and unique properties as a semiconductor material. The high electron mobility, high thermal conductivity, good transparency, wide and direct band gap (3.37 eV), large exciton binding energy (60 meV) at room temperature and easiness of growing it in the nanostructure form, has made it suitable for wide range of applications in optoelectronics, piezoelectric devices, transparent and spin electronics, lasing and chemical sensing. In this thesis, luminescence properties of ZnO nanostructures (nanorods, nanotubes, nanowalls and nanoflowers) are investigated by different approaches for possible future application of these nanostructures as white light emitting diodes. ZnO nanostructures were grown by different growth techniques on different p-type substrates. Still it is a challenge for the researchers to produce a stable and reproducible high quality p-type ZnO and this seriously hinders the progress of ZnO homojunction LEDs. Therefore the excellent properties of ZnO can be utilized by constructing heterojunction with other p-type materials. The first part of the thesis includes paper I-IV. In this part, the luminescence properties of ZnO nanorods grown on different p-type substrates (GaN, 4H-SiC) and different ZnO nanostructures (nanorods, nanotubes, nanoflowers, and nanowalls) grown on the same substrate were investigated. The effect of the post-growth annealing of ZnO nanorods and nanotubes on the deep level emissions and color rendering properties were also investigated. In paper I, ZnO nanorods were grown on p-type GaN and 4H-SiC substrates by low temperature aqueous chemical growth (ACG) method. The luminescence properties of the fabricated LEDs were investigated at room temperature by electroluminescence (EL) and photoluminescence (PL) measurements and consistency was found between both the measurements. The LEDs showed very bright emission that was a combination of three emission peaks in the violet-blue, green and orange-red regions in the visible spectrum. In paper II, different ZnO nanostructures (nanorods, nanotubes, nanoflowers, and nanowalls) were grown on p-GaN and the luminescence properties of these nanostructures based LEDs were comparatively investigated by EL and PL measurements. The nanowalls structures were found to be emitting the highest emission in the visible region, while the nanorods have the highest emissions in the UV region due to its good crystal quality. It was also estimated that the ZnO nanowalls structures have strong white light with the highest color rendering index (CRI) of 95 with correlated color temperature (CCT) of 6518 K. In paper III, we have investigated the origin of the red emissions in ZnO by using post-growth annealing. The ZnO nanotubes were achieved on p-GaN and then annealed in different ambients (argon, air, oxygen and nitrogen) at 600 C for 30 min. By comparative investigations of EL spectra of the LEDs it was found that more than one deep level defects