The In uence of a Magnetic Field on the Formation of Corrosion Defects in Selected Metals and Steels, Analysed Using Positron Annihilation Method
نویسندگان
چکیده
The method of positron lifetime measurement was used to analyse the in uence of a magnetic eld on the kinetics of corrosion defect formation in near-surface layers of iron, titanium as well as S20 and S0H18N9 steel grades. The listed metals, which belong to ferroand paramagnetic materials, have di erent sensitivity to corrosion. It was found that not only the presence of a magnetic eld, but also its direction in uence the dimensions and the concentration of defects formed during corrosion.
منابع مشابه
Calculation of Positron Distribution in the Presence of a Uniform Magnetic Field for the Improvement of Positron Emission Tomography (PET) Imaging Using GEANT4 Toolkit
Introduction Range and diffusion of positron-emitting radiopharmaceuticals are important parameters for image resolution in positron emission tomography (PET). In this study, GEANT4 toolkit was applied to study positron diffusion in soft tissues with and without a magnetic field for six commonly used isotopes in PET imaging including 11C, 13N, 15O, 18F, 68Ga, and 82Rb. Materials and Methods GEA...
متن کاملپایداری سامانه اندازهگیری طول عمر پوزیترون و بررسی نوع و غلظت عیب ناشی از تابش الکترونهای 10 مگا الکترون ولتی بر نمونههای سیلیکونی نوع n و p
Positron annihilation lifetime spectroscopy method with valuation of non-destructive investigation of material, provides information about electron density, defect concentration, type of defects and atoms around the defects. The stability of the system was tested with a source. The time resolution of the whole system has been derived about 365 ps at FWHM. Then n- and p-type silicon samples we...
متن کاملPositron annihilation lifetime spectroscopy in nickel ferrite and iron oxide nanopowders
In this study, a positron annihilation lifetime spectrometer was set up and its resolution was optimized. The spectrometer is a fast-slow arrangement with time resolution of 250 ps. To obtain lifetime components and their intensities from analyzing positron annihilation lifetime spectrum, the Pascual software is used. Positrons are from a source of radioactive 22NaCl with 20 μCi activity enclos...
متن کاملInfluence of Ni Deposition and Subsequent N+ Ion Implantation at Different Implantation Energies on Nano-Structure and Corrosion Behavior of 316 Stainless Steels
Nickel films of 300 nm thickness were deposited by electron beam evaporation at room temperature on 316 stainless steels. Corrosion studies of Ni coated 316 SS have been performed after N+ ion implantation at different energies of 20, 40, 60 and 80 keV. The structure and surface morphology of the films were evaluated using X-ray diffraction (XRD), atomic force microscope (AFM) an...
متن کاملThe Evaluation of Corrosion Behavior of AISI 347 Stainless Steel to ASTM A335 Low Alloy Steel Dissimilar Welds
In the present study, the corrosion behavior of AISI 347 austenitic stainless steel to ASTM A335 low alloy steel dissimilar joint was investigated. For this purpose, two filler metals, ER309L and ERNiCr-3, were selected to be used during the gas tungsten arc welding process. To investigate the corrosion behavior of the joints after welding, the specimens were tested in 3.5% sodium chloride solu...
متن کامل