Effect of austenitising and deformation temperatures on dynamic recrystallisation in Nb-Ti microalloyed steel
نویسندگان
چکیده
An investigation into influence of the austenitising temperature and the austenite deformation temperature on Nb precipitation and recrystallisation kinetics was carried out for a steel containing 0.081C-0.021Ti-0.064Nb (wt. %). The austenite grain structure was correlated to the dispersive properties of Nb atom clustering and precipitation. Irrespective of the austenitising temperature, deformation to 0.75 strain at 1075 °C produced a fully recrystallised microstructure. After deformation at 975 °C, only partial recrystallisation was observed in the samples austenitised at higher temperature, whereas samples austenitised at lower temperature were fully recrystallised. The influence of solute drag and particle pinning effects on the recrystallisation rate is discussed. © (2013) Trans Tech Publications, Switzerland.
منابع مشابه
Determining the Hot Deformation Temperature Range of Medium Carbon Ni-Cr-Mo Low Alloy Steels using Hot Tensile and Hot Torsion Tests
The aim of this study was to investigate the suitable temperature range for hot deformation of three medium carbon Ni-Cr-Mo low alloy steels by hot tensile and hot torsion tests. Hot tensile tests were carried out in the te,prature range of 850-1150°C at a constant strain rate of 0.1 s-1 until fracture. Then, the tensile flow behavior, hot ductility and microstructural evolution of the steels w...
متن کاملتاثیر ترکیب شیمیایی بر تحولات ریزساختاری فولادهای میکروآلیاژی در حین تغییر شکل گرم در منطقه دو فازی (آستنیت + فریت)
Laboratory hot torsion testing technique was carried out on one plain low carbon steel and two plain low carbon Nb and Nb-Ti micro alloyed steels to study the effects of chemical composition, micro alloying addition, on the dynamic softening and grain refinement of ferrite during warm deformation. Deformation schedule was conducted within two phase region (i.e. between Ar3-Ar1). The physical pr...
متن کاملInteraction Between Precipitation and Dynamic Recrystallization in HSLA-100 Microalloyed Steel
Strain induced precipitation in HSLA-100 steel was investigated by conducting hotcompression and relaxation tests at temperature range of 850°C to 1100°C and strain rate of 0.001s-1 to 1s-1. The absence of dynamic recrystallization at temperatures below 1000°C was attributedto the influence of dynamic precipitation. The stress relaxation tests showed that strain inducedprecipitation is possible...
متن کاملEffect of Ti-microalloy Addition on the Formability and Mechanical Properties of a Low Carbon (ST14) Steel
A low carbon Al-killed Ti-added steel was produced in Mobarakeh Steel Complex in Iran. Mechanical properties and microstructural characterizations of steel in the as-cast, hot-rolled, cold-rolled and annealed conditions are presented. Dilatometery tests were carried out to measure the finishing and annealing temperatures of steel. It was found that the addition of small amounts of Ti increas...
متن کاملInfluence of Testing Rate on Lüders Band Propagation in Niobium
S. Rešković, I. Jandrlić, University of Zagreb, Faculty of Metallurgy, Sisak, Croatia, F. Vodopivec Institute of Metals and Technology, Ljubljana, Slovenia Using thermal imaging camera during tensile testing of low carbon and Nb microalloyed steel influence of testing rate on start of plastic deformation was investigated. The results showed that the onset of plastic flow is significantly differ...
متن کامل