Characterization of Al2O3 Films grown by Electron Beam Evaporator on Si Substrates
نویسندگان
چکیده
We report the characterization of aluminum oxide (Al2O3) films which are grown on Si substrates by electron beam evaporator. This paper focuses on the characteristic variation of Al2O3 films depending on the different annealing techniques, such as post-deposition annealing and post-metallization annealing. The capacitance-voltage (C-V) curves indicate a negative charge and interface trap charge density between the Al2O3 film and Si interface. The current-voltage (I-V) curves show a leakage current. The x-ray diffraction (XRD) patterns show the crystallinity of Al2O3 films. Based on the results, the annealing effect is important condition to increase negative fixed charge in the Al2O3 films.
منابع مشابه
Nano-structural Characterization of Post-annealed ZnO Thin Films by X-ray Diffraction and Field Emission Scanning Electron Microscopy
ZnO thin films were deposited on Si(400) substrates by e-beam evaporation technique, and then post-annealed at different annealing temperatures (200-800°C). Dependence of the crystallographic structure, nano-strain, chemical composition and surface physical Morphology of these layers on annealing temperature were studied. The crystallographic structure of films was studied using X-Ray Diffracti...
متن کاملNano-structural Characterization of Post-annealed ZnO Thin Films by X-ray Diffraction and Field Emission Scanning Electron Microscopy
ZnO thin films were deposited on Si(400) substrates by e-beam evaporation technique, and then post-annealed at different annealing temperatures (200-800°C). Dependence of the crystallographic structure, nano-strain, chemical composition and surface physical Morphology of these layers on annealing temperature were studied. The crystallographic structure of films was studied using X-Ray Diffracti...
متن کاملA Study of ZnO Buffer Layer Effect on Physical Properties of ITO Thin Films Deposited on Different Substrates
The improvement of the physical properties of Indium Tin Oxide (ITO) layers is quite advantageous in photovoltaic applications. In this study the ITO film is deposited by RF sputtering onto p-type crystalline silicon (c-Si) with (100) orientation, multicrystalline silicon (mc-Si), and glass substrates coated with ZnO and annealed in vacuum furnace at 400°C. Electrical, optical, structural a...
متن کاملCharacterization of highly-oriented ferroelectric PbxBa1−x TiO3 thin films grown by metalorganic chemical vapor deposition
PbxBa1−xTiO3 (0.2 x 1) thin films were deposited on single-crystal MgO as well as amorphous Si3N4/Si substrates using biaxially textured MgO buffer templates, grown by ion beam-assisted deposition (IBAD). The ferroelectric films were stoichiometric and highly oriented, with only (001) and (100) orientations evident in x-ray diffraction (XRD) scans. Films on biaxially textured templates had smal...
متن کاملMicrostructure of low temperature grown AlN thin films on Si„111..
AlN thin films were grown on HF-etched Si~111! substrates at 400– 600 °C by plasma source molecular beam epitaxy. Reflection high energy electron diffraction and transmission electron microscopy studies show that AlN films grown at 400 °C form an initial amorphous region at the interface, followed by c-axis oriented columnar grains with slightly different tilts and twists. AlN films grown at 60...