Observation of Vortex Lattice Related Anomalies in Polycrystalline YBa2Cu3O7-x Near the Superconducting Transition
نویسنده
چکیده
The d.c. I-V characteristic of polycrystalline YBa2Cu3O7−x high temperature superconductors (HTSC) is measured near the transition temperature (Tc). The Tc was found to be 90 K with a width of 2 K. The voltage was measured at various current values and with reversing the current. A difference in voltage was found for forward and reverse current directions near Tc. The observed directionality of the I-V characteristic can be understood in terms of quantized magnetic flux by the self-field of the current and the proximity junctions in these materials. This can also be understood qualitatively as due to the d-wave superconductivity. The measured dc voltage showed increased noise near Tc which is possibly related to 1/f noise due to the motion of Abrikosov flux lines.
منابع مشابه
خواص ترابردی مغناطیسی واثر هال در نمونه هایGdpr-123
Single phase polycrystalline Gd1-xPrxBa2Cu3O7-δ samples with x=0.05 , 0.10, and 0.15 have been prepared by standard solid state reaction technique and characterized by XRD and SEM analysis. The electrical resistivity, Hall effect and magnetoresistance measurements have been on the samples. The electrical resistivity measurements indicate a reduction of transition temperature (Tc) and an incre...
متن کاملساخت نانو بلورکهای δ-7O3Cu2YBa به روش مکانوشیمیایی و بررسی دمای گذار ترکیبات -7O3Cu2YBa(x-1) + 2 xMnO (02/0 ،015/0 ،01/0 ،005/0 ،0 = x)
In this research, YBa2Cu3O7-d (0 < d < 1) nanocrystalite superconductor was prepared by mechanochemical alloying method. We synthesized YBa2Cu3O7-d via mixing the BaCO3, Y2O3, CuO powders and milling in SPEX 8000 for 5h with weight ratio of ball to powder 10:1 and steel balls of 11mm diameter, followed by heating for 4h at 850 ˚C. The superconductor phase formation process was completed with si...
متن کاملEffect of high-intensity ultrasound on superconducting properties of polycrystalline YBa2Cu3O7−x
High intensity ultrasonic irradiation (sonication) of alkane slurries of polycrystalline YBa2Cu3O7−x leads to a significant modification of the grain morphology and, if performed with enforced oxygen flow, results in the increase of the superconducting transition temperature. Sonication with added Fe(CO)5 produces magnetic Fe2O3 nanoparticles deposited on the surface of YBa2Cu3O7−x (YBCO) granu...
متن کاملExperimental aspects of Alpha, Beta angles distortion on superconductivity in 1111-type Iron-based superconductor
In this research, we aim to clarify the relationship between the structural distortion due to doping and the superconductivity existence in the FeAs4 structure. For this, we have prepared polycrystalline of NdFeAsO0.8F0.2, NdFeAs0.95Sb0.05O0.8F0.2 and Nd0.99Ca0.01FeAsO0.8F0.2 samples by one-step solid state reaction method. The structural and electrical properties of the samples were characteri...
متن کاملOBSERVATION OF NONUNIFORM CURRENT TRANSPORT IN EPITAXIAL YBa2Cu3O7– x FILM NEAR THE SUPERCONDUCTING TRANSITION TEMPERATURE
We have studied the local transport properties in an epitaxial YBa2Cu3O7 x (YBCO) film on LaAlO3 (LAO) using variable temperature scanning laser microscope (VTSLM) near the superconducting transition. A map of the superconducting transition temperature ðT c Þ is generated from a series of VTSLM images. The map of T c indicates there are inhomogeneities in the film large enough to create nonunif...