The influence of surface currents on pattern-dependent charging and notching
نویسندگان
چکیده
Surface charge dissipation on insulator surfaces can reduce local charging potentials thereby preventing ion trajectory deflection at the bottom of trenches that leads to lateral sidewall etching ~notching!. We perform detailed Monte Carlo simulations of pattern-dependent charging during etching in high-density plasmas with the maximum sustainable surface electric field as a parameter. Significant notching occurs for a threshold electric field as low as 0.5 MV/cm or 50 V/mm, which is reasonable for the surface of good insulators. The results support pattern-dependent charging as the leading cause of notching and suggest that the problem will disappear as trench widths are reduced. © 1998 American Institute of Physics. @S0021-8979~98!04614-3#
منابع مشابه
How tunneling currents reduce plasma-induced charging
As semiconductor manufacturing moves towards smaller logic devices and thinner gate oxides, there is serious concern that pattern-dependent charging during plasma etching will impede progress by distorting etch profiles and by causing oxide breakdown. Simulations of the final overetch predict that the use of ultrathin oxides (<5 nm), combined with a low substrate potential, will actually elimin...
متن کاملElectron irradiance of conductive sidewalls: A determining factor for pattern-dependent charging
Numerical simulations of charging and profile evolution during gate electrode overetching in high density plasmas have been performed to investigate the effect of long conductive sidewalls on profile distortion ~notching!. The results reveal that the angle of electron irradiance of the conductive portion of the sidewalls affects profoundly the charging potential of the gates. Larger angles, obt...
متن کاملModeling of charging damage during interlevel oxide deposition in high-density plasmas
Monte Carlo simulations of pattern-dependent charging during interlevel dielectric ~ILD! deposition in high-density plasmas reveal that the initial conformality of the ILD film plays a crucial role in metal line charging up and the subsequent degradation to the buried gate oxide to which the metal line is connected. Line charging occurs when the top dielectric is thick enough to prevent tunneli...
متن کاملOn the link between electron shadowing and charging damage
Charging and topography evolution simulations during plasma etching of high aspect ratio line-and-space patterns reveal that electron shadowing of the sidewalls critically affects charging damage. Decreasing the degree of electron shadowing by using thinner masks decreases the potentials of the etched features with a concomitant reduction in Fowler–Nordheim tunneling currents through underlying...
متن کاملOn the Origin of Charging Damage during Etching of Antenna Structures
Monte Carlo simulations of charging and profile evolution in patterned antenna structures during etching in high-density plasmas reveal a rapid change in the potential of the lines at end point, which causes a surge in electron tunneling through thin gate oxides and possibly charging damage. The condition of the substrate (grounded vs. floating) determines the magnitude of the surge and whether...