Effect of Thermal Aging on the Impact Strength of Soldered Bumps under Formic Acid Atmosphere
نویسندگان
چکیده
In this study, we have investigated the effect of thermal aging on impact strength of Sn-Ag-Cu solder bumps in fluxless soldering process using formic acid atmosphere. We conducted impact tests on as-reflowed and thermally-aged solder bumps, which were fabricated on either formic acid atmosphere or a liquid flux. The results indicated that the morphology of the intermetallic compound layers in samples soldered using formic acid was similar to those soldered with the liquid flux, after soldering and after thermal aging. The fluxless solder bumps, using formic acid atmosphere, have impact strengths similar to the solder bumps obtained using the liquid flux in nitrogen atmosphere
منابع مشابه
Formic Acid Decomposition Using Synthesized Ag/TiO2 Nanocomposite in Ethanol-Water Media Under Illumination of Near UV Light
The effect of ethanol-water media on the synthesis of Ag/TiO2 nanocomposite was investigated with 0.05, 0.1 and 0.5 (wt.%) of Ag content. Ethanol was used as hole-scavenger enhancing the photodecomposition of Ag+ ions under illumination of near-UV light. The nanocomposites were further calcined to 300˚C and 400˚C under controlled atmosphere. The synthesized nanocomposites were tested for photoc...
متن کاملEnvironmental effects on mechanical properties of glass/epoxy and fiber metal laminates, Part II: Isothermal aging
The aim of this study is to investigate effects of isothermal aging on mechanical properties of fiber metal laminates (FMLs) and glass/epoxy composites. For this purpose, both materials were fabricated using the wet lay-up manufacturing technique under vacuum pressure. Both the glass/epoxy composites and the FML specimens were then subjected to isothermal aging (130°C, dried air) for up to 5 we...
متن کاملEffect of Thermal and Mechanical Aging on Flexural Strength of Zirkonzahn and Mamut Zirconia Ceramics
Objective: Despite the high strength of zirconia restorations, aging in the oral environment and masticatory loading may result in transformation of tetragonal to monoclinic phase and decrease their strength. Statements in this regard are controversial. This study sought to compare the flexural strength (FS) of Zirkonzahn (ZirkonZahn, Cercon, Ceramill) and Mamut (Dubai Medical Equipment LLC, ...
متن کاملEffect of Functionalization Process on Thermal Conductivity of Graphene Nanofluids
In this research, Graphene was synthesized by chemical vapor deposition (CVD) method in atmosphere pressure (14.7 psi). Different functionalization method was used for oxidizing of graphene such as acid and alkaline treatments. The Functionalized graphene (FG) was characterized by FTIR and Raman spectroscopy. Nanofluid with water and different concentration (0.05, 0.15 and 0.25 wt %) of ...
متن کاملEffect of Salicylic Acid on Antioxidant Enzyms of Milk Thistle (Silybum marianum) Accelerated Aging Seed
Effects of accelerated aging and seed priming treatments were studied on milk thistle seeds during germination process. Experiment was performed in a factorial based on Complete Randomized Design (CRD). Treatments were Salicylic acid concentrations (0, 500, 1000, 1500 and 2000 ppm) and accelerated aging for (0, 48, 96 and 144 hours under 45 °C and 95% humidity) with three replications. Our ...
متن کامل