Self-healing polymers, based on microencapsulated dicyclopentadiene and Grubbs' catalyst embedded in the polymer matrix, are capable of responding to propagating fatigue cracks by autonomic processes that lead to higher endurance limits and life extension, or even the complete arrest of the crack growth. The amount of fatigue-life extension depends on the relative magnitude of the mechanical kinetics of crack propagation and the chemical kinetics of healing. As the healing kinetics are accelerated, greater fatigue life extension is achieved. The use of wax-protected, recrystallized Grubbs' catalyst leads to a fourfold increase in the rate of polymerization of bulk dicyclopentadiene and extends the fatigue life of a polymer specimen over 30 times longer than a comparable non-healing specimen. The fatigue life of polymers under extremely fast fatigue crack growth can be extended through the incorporation of periodic rest periods, effectively training the self-healing polymeric material to achieve higher endurance limits.
منابع مشابه
Retardation and repair of fatigue cracks in a microcapsule toughened epoxy composite—Part II: In situ self-healing
Successful arrest and retardation of fatigue cracks is achieved with an in situ self-healing epoxy matrix composite that incorporates microencapsulated dicyclopentadiene (DCPD) healing agent and Grubbs first generation Ru catalyst. Healing agent is released into the crack plane by the propagating crack, where it polymerizes to form a polymer wedge, generating a crack tip shielding mechanism. Du...
متن کاملSelf-healing concrete and environmental health
Nanotechnology will serve as a suitable solution to achieve high performance in future construction and construction. Using this new technology, creativity and innovation can be achieved in the building industry. one of these new technologies of smart concrete is that in recent years, many researches and experiments have been done in scientific research centers around the world, so that the con...
متن کاملQuantification of the Service Life Extension and Environmental Benefit of Chloride Exposed Self-Healing Concrete
Formation of cracks impairs the durability of concrete elements. Corrosion inducing substances, such as chlorides, can enter the matrix through these cracks and cause steel reinforcement corrosion and concrete degradation. Self-repair of concrete cracks is an innovative technique which has been studied extensively during the past decade and which may help to increase the sustainability of concr...
متن کاملRetardation and repair of fatigue cracks in a microcapsule toughened epoxy composite – Part I: Manual infiltration
As a first step towards a new crack healing methodology for cyclic loading, this paper examines two promising crack-tip shielding mechanisms during fatigue of a microcapsule toughened epoxy. Artificial crack closure is achieved by injecting precatalyzed monomer into the crack plane to form a polymer wedge at the crack tip. The effect of wedge geometry is also considered, as dictated by crack lo...
متن کاملThe effectiveness of self-healing training on job burnout, quality of life, and emotional flexibility in Isfahan's social emergency personnel
Background and aims: Burnout is one of the most important unavoidable consequences of work stress that causes physical fatigue, changes in job behavior and performance. The purpose of the present study was to investigate the effectiveness of self-healing training on job burnout, quality of life, and emotional resilience of Isfahan's social emergency personnel. Methods: The research metho...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Journal of the Royal Society, Interface
دوره 4 13 شماره
صفحات -
تاریخ انتشار 2007