IRG/WP 09-50262 THE INTERNATIONAL RESEARCH GROUP ON WOOD PROTECTION Section 5 Sustainability and environment Rapid Microwave-Assisted Acid Extraction of Metals from Chromated Copper Arsenate (CCA)-Treated Southern Pine Wood
نویسندگان
چکیده
The effects of acid concentration, reaction time, and temperature in a microwave reactor on recovery of CCA-treated wood were evaluated. Extraction of copper, chromium, and arsenic metals from chromated copper arsenate (CCA)-treated southern pine wood samples with three different acids (i.e., acetic acid, oxalic acid, and phosphoric acid) was investigated using in microwave reactor. Oxalic acid was effective in removing 100% of the chromium and arsenic at 160°C and 30 min., and acetic acid could remove 98% of the copper and arsenic at the same conditions. Oxalic acid greatly improved the extraction efficiency of arsenic and chromium when time was prolonged from 10min. to 30min. Acetic acid also showed improved ability to remove arsenic and copper when the reaction temperature was increased from 90°C to 160°C. Keyword: CCA, recovery, microwave, extraction
منابع مشابه
Rapid microwave-assisted acid extraction of southern pine waste wood to remove metals from chromated copper arsenate (CCA) treatment
Recovery of metals from chromated copper arsenate (CCA)-treated southern pine wood particles was investigated by extraction in a microwave reactor with binary combinations of acetic acid (AA), oxalic acid (OxA), and phosphoric acid (PhA). Use of OxA was not successful, as insoluble copper oxalate complexes impeded copper removal. The combination of OxA and AA also had adverse effects on copper ...
متن کاملNew Approach to Remove Metals from Chromated Copper Arsenate (CCA)-Treated Wood
Recovery of metals from chromated copper arsenate (CCA)-treated southern pine wood particles was investigated using binary acid solutions consisting of acetic, oxalic, and phosphoric acids in a microwave reactor. Formation of an insoluble copper oxalate complex in the binary solution containing oxalic acid was the major factor for low copper removal. Furthermore, the possible complexation of ac...
متن کاملProperties of particleboard made from recycled CCA-treated wood
Recovery of chromated copper arsenate (CCA)-treated wood for reuse has been the focus of several international research groups due to the imminent disposal problem created when large quantities of CCA-treated wood ultimately come out of service. Bioleaching with Bacillus licheniformis CC01 and oxalic acid extraction are two methods known to remove significant quantities of metals from CCA-treat...
متن کاملFractionation of heavy metals in liquefied chromated copper arsenate 9-treated wood sludge using a modified BCR-sequential extraction procedure.
Chromated copper arsenate (CCA)-treated wood was liquefied with polyethylene glycol/glycerin and sulfuric acid. After liquefaction, most CCA metals (98% As, 92% Cr, and 83% Cu) were removed from liquefied CCA-treated wood by precipitation with calcium hydroxide. The original CCA-treated wood and liquefied CCA-treated wood sludge were fractionated by a modified Community Bureau of Reference (BCR...
متن کاملComparative Study on Liquefaction of Creosote and Chromated Copper Arsenate (CCA)-treated wood and Untreated Southern Pine Wood: Effects of Acid Catalyst Content, Liquefaction Time, Temperature, and Phenol to Wood Ratio
Creosoteand chromated copper arsenate (CCA)-treated wood waste and untreated southern pine wood were liquefied with phenol and sulfuric acid. The effects of sulfuric acid content, liquefaction time, liquefaction temperature, and phenol to wood ratio on liquefaction rate (i.e., wood residue content) were investigated and analyzed by analysis of variance (ANOVA). The results showed that both creo...