Protective effect of different tetrafluorides on erosion of pellicle-free and pellicle-covered enamel and dentine.

The aim was to analyze the protective effects of titanium, zirconium and hafnium tetrafluorides on erosion of pellicle-free and pellicle-covered enamel and dentine in vitro. Eight groups of 20 specimens each of bovine enamel and bovine dentine were prepared. Half the specimens in each group were immersed in human saliva for 2 h for pellicle formation. Specimens were then left untreated (controls) or were treated for 120 s with TiF(4), ZrF(4) or HfF(4) solutions (0.4 or 1%) or 1.25% AmF/NaF gel. All specimens were eroded by exposure to hydrochloric acid, pH 2.6, for 25 min. Cumulative calcium release into the acid was monitored in consecutive 30-second intervals for 5 min, then at 2-min intervals up to a total erosion time of 25 min using the Arsenazo III procedure. Data were analyzed by ANOVA. 1% TiF(4) solution offered the best protective effect, especially in dentine (reduction of calcium loss about 50% at 25 min). 1% ZrF(4), 1% HfF(4) and 0.4% TiF(4) also reduced calcium loss, but to a lesser extent. Long-term effects were limited to dentine, while reduction of enamel erosion (about 25%) was restricted to 1-min erosion. The fluoride gel had a protective effect only in dentine. The efficacy of the tetrafluorides was influenced by the presence of the pellicle layer, in that the protection against dentine erosion by TiF(4) and ZrF(4) was greater on pellicle-covered specimens. Tetrafluoride solutions, especially 1% TiF(4), could decrease dental erosion, but were more effective on dentine than on enamel.