Phase transformations and thermodynamic properties of nanocrystalline FePt powders
نویسندگان
چکیده
The solid state reactions and structural evolution in nanocrystalline FePt powders during mechanical ball milling at 77 K and subsequent annealing have been investigated. Above 310 °C the formation of L10 FePt is observed. As the milling time increases, the enthalpy evolved during the transformations is reduced, whereas the corresponding activation energy increases. For accelerating the ordering process a fi ne lamellar structure of Fe and Pt is favourable.
منابع مشابه
Characterization and Phase Transformation of Spherical YSZ Powders Fabricated Via air Plasma Spray Method
Air plasma spray (APS) process is used to produce high density and flowability spherical powders. Phase transformation that occurred in this process isn’t well known. In this paper, the YSZ powders have been sprayed in water to investigate the morphology changes and phase transformations via air plasma spray (APS) method. Phase analysis of powders was examined by XRD and the crystallite size an...
متن کاملEffect of Heat Treatment on Structural and Magnetic Properties of Nanocrystalline SrFe12O19 Hexaferrite synthesized by Co-Precipitation Method
Nanocrystalline strontium hexaferrite (SrFe12O19) powders have been successfully synthesized using the facile Co-precipitation method. The ferrite precursors were achieved from mixtures of strontium and ferric chloride in an aqueous medium without any surfactant and soft template. The as-received powders were calcined at 800 and 1000 ˚C for 2 hours in air. The final powders were characterized b...
متن کاملMagnetic and Electrical Properties of Nanocrystalline Fe85Si10Ni5/Phenolic Resin Soft Magnetic Composites
In this work, nanocrystalline Fe85Si10Ni5 soft magnetic powders were prepared by mechanical alloying and subsequent annealing to reduce the internal stresses and lattice strains. The powders were mixed with phenolic resin and warm pressed to produce nanostructured soft magnetic composites. The effect of annealing time and temperature on the crystalline structure, microstructure and magnetic pro...
متن کاملThermodynamic analysis of nanocrystalline solid solution formation in the W-Co-Si ternary system by mechanical alloying
Co3W2Si intermetallic compound was synthesized by mechanical alloying (MA) of W, Co and Si elemental powder mixtures. The phase composition of the milled products was evaluated by X-ray diffraction (XRD) analysis. Morphological evolutions were characterized by transmission electron microscopy (TEM). The results showed that high energy ball milling performed in the present work led to the format...
متن کاملEffect of Milling Time on Hydrogen Desorption Properties of Nanocrystalline MgH2
Nanocrystalline magnesium hydride powder was synthesized by mechanical milling of MgH2 in a planetary ball mill for various times. The effect of MgH2 structure, i.e. crystallite size, lattice strain, particle size and specific surface area on the hydrogen desorption properties was investigated. A single peak of hydrogen desorption was observed for as-received powder, exhibiting an average parti...