The Strengthening Effect of Phase Boundaries in a Severely Plastically Deformed Ti-Al Composite Wire
نویسندگان
چکیده
An accumulative swaging and bundling technique is used to prepare composite wires made of Ti and an Al alloy. These wires show reasonable higher yield stresses than expected from the pure material flow curves. The additional strengthening in the composite is analyzed using nanoindentation measurements, tensile testings and investigations of the microstructure. In addition, these properties are analyzed in relation to the fracture surface of the mechanically tested wires. Additional strengthening due to the presence of phase boundaries could be verified. Indications for residual stresses are found that cause a global hardness gradient from the center to the wire rim. Finally, the yield stress of the wires are calculated based on local hardness measurements.
منابع مشابه
Pii: S1359-6462(99)00345-0
In a recent paper, Li and Wawner [1] reported results of a study of the interaction between dislocations and {111}a precipitate plates of V (Al2Cu) phase in a plastically deformed Al-Cu-Mg-Ag alloy using both conventional and high resolution transmission electron microscopy (HRTEM). Based on experimental observations that V phase was sheared in plastically-deformed samples, they propose a stren...
متن کاملEffect of Pre-existing Nano Sized Precipitates on Microstructure and Mechanical Property of Al-0.2wt% Sc Highly Deformed by ARB Process
The effect of pre-existing nano sized precipitates on the mechanisms and rate of grain refinement has been investigated during the severe plastic deformation. A binary Al–0.2Sc alloy, containing coherent Al3Sc particles, of 3.62 nm in diameter has been deformed by accumulative roll bonding up to 10 cycles. The resulting deformed structures were quantitatively analyzed using electron backscatter...
متن کاملEvaluating the Effect of the Number of Welding Passes on Microstructure, Hardness and Residual Stress of Ti-Al-Si Composite Coatings
The purpose of the present work is to investigate the influence of the number of weld-passes on microstructure, hardness and residual stresses of composite coatings composed of Ti-Al-Si intermetallic compounds. In this regard, surface coating of pure Ti was carried out using one and two passes of tungsten inert gas (TIG) welding with an Al filler alloy (grade 4043). Phase and structural evaluat...
متن کاملDISLOCATIONS STRUCTURE AND SCATTERING PHENOMENON IN CRYSTALLINE CELL SIZE OF 2024 AL ALLOY DEFORMED BY ONE PASS OF ECAP AT ROOM TEMPERATURE
Variation in microstructural features of 2024 aluminum alloy plastically deformed by equal channel angular pressing (ECAP) at room temperature, was investigated by X-Ray diffraction in this work. These include dislocation density dislocation characteristic and the cell size of crystalline domains. Dislocations contrast factor was calculated using elastic constants of the alloy such as C 11, C 2...
متن کاملALUMINOTHERMIC-CARBOTHERMAL REDUCTION SYNTHESIS OF NANO CRYSTALLINE Al2O3-Ti(C,N) COMPOSITE WITH DIFFERENT BED TYPES
Ceramic-matrix composites containing TiC-TiN have been used in a variety of application because of their superior properties such as high hardness, good wear resistance and high chemical stability. In this research, effect of coke and coke/calcium beds in synthesis of Al 2O3-Ti(C, N) composites using alumino-carbothermic reduction of TiO 2 has been investigated. Al, TiO 2 and active ca...
متن کامل