IR Li2Ga2GeS6 nanocrystallized GeS2-Ga2S3-Li2S electroconductive chalcogenide glass with good nonlinearity
نویسندگان
چکیده
GeS(2)-Ga(2)S(3)-Li(2)S electroconductive glasses were prepared by the conventional melt-quenching method through carefully controlling the heating rate. Comparing with the reference of glass-forming region, our investigated GeS(2)-Ga(2)S(3)-Li(2)S system was extended to the cation ratio of 0-20% Li with around 40% Ga. GeS(2)-Ga(2)S(3)-Li(2)S glass-ceramics containing IR Li2Ga2GeS6 nonlinear nanocrystals were obtained by the more carefully controlled heating rate. Its optical nonlinearity was investigated by the Maker fringe measurements, the maximum second harmonic intensity was observed to be 0.35 of the reference Z-cut quartz. IR Li(2)Ga(2)GeS(6) nonlinear crystals were directly obtained at the composition of 40GeS(2)-30GaS(1.5)-30LiS(0.5).
منابع مشابه
Second-order optical nonlinearity and ionic conductivity of nanocrystalline GeS2-Ga2S3-LiI glass-ceramics with improved thermo-mechanical properties.
IR-transparent chalcogenide glass-ceramics were fabricated through a careful ceramization process of the as-prepared 65 GeS(2) x 25 Ga(2)S(3) x 10 LiI glasses at a temperature of 403 degrees C for various durations. Owing to the precipitation of Li(x)Ga(y)S(z) crystals with a Ga(2)S(3)-like structure, clear second-harmonic generation was observed in the sample crystallized at 403 degrees C for ...
متن کاملRsc_cp_b921909a 3780..3787
IR-transparent chalcogenide glass-ceramics were fabricated through a careful ceramization process of the as-prepared 65GeS2 25Ga2S3 10LiI glasses at a temperature of 403 1C for various durations. Owing to the precipitation of LixGaySz crystals with a Ga2S3-like structure, clear second-harmonic generation was observed in the sample crystallized at 403 1C for 60 h, which has a greatly improved re...
متن کاملGeS2–In2S3–CsI Chalcogenide Glasses Doped with Rare Earth Ions for Near- and Mid-IR Luminescence
Chalcogenide glass has been considered as a promising host for the potential laser gain and amplifier media operating in near- and mid-IR spectral region. In this work, the IR luminescence spectra of rare earth ions (Tm3+, Er3+, and Dy3+) doped 65GeS2-25In2S3-10CsI chalcogenide glasses were measured under the excitation of an 808 nm laser diode. To the best of our knowledge, it firstly provides...
متن کاملInfluence of the cooling-rate on the glass transition temperature and the structural properties of glassy GeS2: an ab initio molecular dynamics study
Using density-functional molecular dynamics simulations we analyzed the cooling-rate effects on the physical properties of GeS2 chalcogenide glasses. Liquid samples were cooled linearly in time according to T (t) = T0 − γt where γ is the cooling rate. We found that our model leads to a promising description of the glass transition temperature Tg as a function of γ and gives a correct Tg for exp...
متن کاملGa-La-S-Se glass for visible and thermal imaging
Chalcogenide glasses are emerging as important enabling materials for low-cost infrared imaging by virtue of their transparency in the key short-wave infrared (SWIR) to long-wave infrared (LWIR) bands and the ability to be mass produced and molded into near-net shape lenses. In this paper, we introduce a new family of chalcogenide glasses, which offer visible as well as infrared transmission an...
متن کامل