UV-LED Curing Efficiency of Wood Coatings
نویسندگان
چکیده
Ultraviolet light emitting diodes (UV-LEDs) have attracted great interest in recent years. They can be used to polymerize coatings, such as those used for prefinished wood flooring. In this project, two lamps were compared for their suitability to be used on a wood flooring finishing line: a UV-microwave and a UV-LED lamp. Low heat emission was found for the UV-LED lamp compared to the UV-microwave one. This study also reveals that the 4 W/cm2 UV-LED lamp used is not powerful enough to cure UV high solids acrylate coatings while satisfactory results can be obtained for UV water-based formulations. In fact, conversion percentages were found to be low for the high solids coatings, leaving the coatings tacky. Higher conversion percentages were obtained for the UV water-based formulations. As a result, mass loss, hardness, and scratch resistance found for the samples cured by UV-LED were closed to the ones found for the samples cured using the UV microwave lamp.
منابع مشابه
Synergistic Effect of Addition of Fillers on Properties of Interior Waterborne UV-Curing Wood Coatings
A waterborne ultraviolet (UV)-curing coating was prepared on the surface of wood materials with modification of talcum powder and calcium carbonate (CaCO3). When the waterborne UV-curing coatings on the surface of wood materials (WUVCW) was radiated for 1 min by UV (λ = 365 nm) and dried at 40 ◦C for 10 min, it showed good hardness, adhesion, and impact strength, with controlling the talcum con...
متن کاملUV Curing of Pigmented High-Build Wood Coatings Based on Non-Air-Inhibited Unsaturated Polyesters
متن کامل
Characterizing the Efficiency of UV LED Curing
This paper examines the effects of some key operating parameters of UV sources on the curing of various UV inks, coatings and adhesives. The effects of peak UV wavelength and peak intensity are quantitatively evaluated using FT-IR. The data are helpful in guiding both formulators, raw material suppliers and end users to better understand the impact of the UV sources, especially UV LED sources, ...
متن کاملStudy the curing behavior and mechanical properties of Pigmented UV curable epoxy acrylate monomers
The formulations contained different acrylate monomer with different structure and functionalities and TiO2, were applied to obtain pigmented acrylic films by UV exposure. The conversion and mechanical characteristic were correlated. The results showed that there is a significant interaction between pigment, reactive diluents’ type and mechanical properties of coatings. It seems that cured film...
متن کاملSynthesis and characterization of novel dual UV/thermal curable epoxy rosinate
Rosin has a comprehensive application in adhesives, printing inks, protective coatings, rubbers and pharmaceutical. In this work, novel dual UV/thermal curable epoxy rosinate was synthesized by esterification reaction between epoxy resin and purified rosin. This product was evaluated by FT-IR spectroscopy techniques and acid number. UV curable resin was formulated for UV curing ability by benzo...