Classification of corrosion defects in NiAl bronze through image analysis
نویسندگان
چکیده
Corrosion surface damage in the form of pitting and micro-cracks is observed in many metals. Cracks usually initiate from the pits and grow under cyclic stresses and eventually lead to material failure. An image analysis based on wavelet transforms and fractals was used to study the corrosion morphology of nickel aluminum bronze metal under varying corrosion conditions and applied stresses. Image feature parameters were extracted and analyzed to classify the pits/cracks in the metal samples. The results obtained indicate that classification of pits/cracks is possible with image analysis and may be used for correlating service/failure conditions based on corrosion morphology. 2010 Elsevier Ltd. All rights reserved.
منابع مشابه
فن شناسی و آسیب شناسی دو خنجر مفرغی از هزارۀ دوم قبل از میلاد متعلق به محوطۀ باستانی گَروی
The objects of the study are two bronze daggers dated back to the late Bronze Age and early Iron Age. They lack any ornaments and there is corrosion and oxidation in their surface. The purpose of this study is to recognize the technological and pathological research on the mentioned objects through comparative and pathological studies and library method, to conduct the technological and patholo...
متن کاملFabricating Superior NiAl Bronze Components through Wire Arc Additive Manufacturing
Cast nickel aluminum bronze (NAB) alloy is widely used for large engineering components in marine applications due to its excellent mechanical properties and corrosion resistance. Casting porosity, as well as coarse microstructure, however, are accompanied by a decrease in mechanical properties of cast NAB components. Although heat treatment, friction stir processing, and fusion welding were im...
متن کاملبررسی روند تشکیل ترکیبات اکسیدی در آثار برنزی با استناد به مطالعات میکروسکوپی
Due to the complex corrosion mechanism of the bronze objects, explaining the structure of different layers of corrosion in these objects at microscopic levels is possible. Typically copper oxide(I) is the first corrosion layer on surface of bronze objects that are excavated of historical sites. However, depending on the environmental conditions، various forms of corrosion layer of tin or copper...
متن کاملتحلیل بحران برپایۀ سنجش عوامل مؤثر بر خوردگی فعال و ارزیابی بحران در مجموعه‌های برنزی باستانی
Recently risk assessment and management in cultural-historical collections is one of the important subjects in the field of preventive conservation research. Different methods and aspects of are used and studied in the field of risk assessment in archaeological sites and collections and significant results are achieved and published in last decades. One of the types of archaeological collection...
متن کاملOccurrence of phosphatic corrosion products on bronze swords of the Warring States period buried at Lijiaba site in Chongqing, China
Corrosion products on three bronze swords found in tombs dating from the Warring States period at Lijiaba site, Yunyang county, Chongqing were characterized by Raman and X-ray fluorescence spectroscopies. The major corrosion products were cuprite, malachite, cerussite and cassiterite, along with the copper and lead phosphates, libethenite and pyromorphite. The presence of libethenite and pyromo...