Effects of Aluminum Sputtering on the Corrosion Resistance of Az91 Alloy Wpływ Glinu Nanoszonego Metodą Rozpylania Jonowego Na Odporność Stopu Az91 Na Korozję

The corrosion resistance of a Magnesium alloy is low and needs to be improved. This research aimed at corrosion-resistance improvement by supatterd deposition aluminium film, which is formed on the surface of AZ91 Magnesium-alloy. Corrosion resistance performed polarization curve measurement, was evaluated in quest of the corrosion rate using the Tafel extrapolation method, and conducted surface observation and EDS analysis by SEM. Although corrosion resistance is not improved only by film forming because of defects in film, corrosion resistance is improved by heat treatment for 3 hours by 553K after sputtering. In the case of heat treated at 623K and 673K for 3 hours, magnesium diffuses through the alminium film and reached the surface of the film. Thus, heat treatment at high temperature degrade the corrosion resistance of the film. The optimization of heat treatment after sputtering is important in this method.