Anisotropic Vapor HF etching of silicon dioxide for Si microstructure release
نویسندگان
چکیده
Damages are created in a sacrificial layer of silicon dioxide by ion implantation to enhance the etch rate of silicon-dioxide in liquid and vapor phase hydrofluoric acid. The etch rate ratio between implanted and unimplanted silicon dioxide is more than 150 in vapor hydrofluoric acid (VHF). This feature is of interest to greatly reduce the underetch of microelectromechanical systems anchors. Based on the experimentally extracted etch rate of unimplanted and implanted silicon dioxide, the patterning of the sacrificial layer can be predicted by simulation.
منابع مشابه
Etching characteristics of Si{110} in 20 wt% KOH with addition of hydroxylamine for the fabrication of bulk micromachined MEMS
Anisotropic wet etching is a most widely employed for the fabrication of MEMS/NEMS structures using silicon bulk micromachining. The use of Si{110} in MEMS is inevitable when a microstructure with vertical sidewall is to be fabricated using wet anisotropic etching. In most commonly employed etchants (i.e. TMAH and KOH), potassium hydroxide (KOH) exhibits higher etch rate and provides improved a...
متن کاملThe Etching of Silicon Nitride in Phosphoric Acid with Silicon Dioxide as a Mask
The water content of phosphoric acid in etching silicon nitride and silicon dioxide plays an important role. An increase in water content increases the etch rate of silicon nitride and decreases the etch rate of silicon dioxide. The highest possible temperature for a fixed water content at atmospheric pressure in the system H2O-P2O5 is realized by boiling the liquid and refluxing the vapor phas...
متن کاملSurface Micromachining for Microelectromechanical Systems
Surface micromachining is characterized by the fabrication of micromechanical structures from deposited thin films. Originally employed for integrated circuits, films composed of materials such as low-pressure chemical-vapor-deposition polycrystalline silicon, silicon nitride, and silicon dioxides can be sequentially deposited and selectively removed to build or “machine” three-dimensional stru...
متن کاملFabrication of p-Type Nano-porous Silicon Prepared by Electrochemical Etching Technique in HF-Ethanol and HF-Ethanol-H2O Solutions
Nano-porous silicon were simply prepared from p-type single crystalline silicon wafer by electrochemical etching technique via exerting constant current density in two different HF-Ethanol and HF-Ethanol-H2O solutions. The mesoporous silicon layers were characterized by field emission scanning electron microscopy and scanning electron microscopy. The results demonstrate that the width of nano-p...
متن کاملFabrication of MEMS devices by using anhydrous HF gas-phase etching with alcoholic vapor
In silicon surface micromachining, anhydrous HF GPE process was verified as a very effective method for the dry release of microstructures. The developed gas-phase etching (GPE) process with anhydrous hydrogen fluoride (HF) gas and alcoholic vapor such as methanol, isopropyl alcohol (IPA) was characterized and its selective etching properties were discussed. The structural layers are P-doped mu...
متن کامل