Microwave-Absorbing Characteristics and XRD Characterization of Magnetic Separation Products of Reductive Products of Ilmenite Concentrate
نویسندگان
چکیده
The microwave absorbing characteristics of magnetic separation products (magnetic and non-magnetic) of reductive products of ilmenite concentrate were measured by the method of microwave cavity perturbation and the magnetic separation products were characterized by X-Ray Diffraction (XRD). It was demonstrated that metallic iron was a strong microwave absorbing material, while TiO2 was a weak microwave absorbing material. The decrease of a strong microwave absorbing material and an increase of weak microwave absorbing material resulted in the great decrease of microwave absorbing characteristics of magnetic products by using a current intensity from 2.5 to 3.0 A. FeTi2O5 was a strong microwave absorbing material, the increasing content would lead to the significant increase of the microwave absorbing characteristics of non-magnetic products by using a current intensity from 2.0 to 4.0 A. The conclusions could help us to optimize the ilmenite concentrate processing by microwaves and microwave cavity design.
منابع مشابه
Investigation on magnetic and microwave behavior of magnetite nanoparticles coated carbon fibers composite
Radar absorbing materials, i.e. magnetite (Fe3O4) coated carbon fibers (MCCFs) were fabricated by electro-deposition technique. Black-colored single spinel phase Fe3O4 nanoparticles was easily synthesized by hydrothermal method using reduction of a Fe (III) - Triethanolamine complex in an aqueous alkaline solution at 60-80 ◦C. Uniform and compact Fe3O4 films were fabricated on nitric acid treat...
متن کاملBeneficiation of Low-Grade Laterite Nickel by Calcination-Magnetic Separation Method
In this research, Effect of thermal treatment on beneficiation of low-grade laterite nickel by calcination-magnetic separation method was studied. In order to determine the components and elements of the sample, to recognize the main and minor minerals and their bond, and phase transformation caused by thermal treatment, Chemical analysis (XRF and ICP), microscopic studies and XRD analysis ...
متن کاملBiosynthesis and Study of Microwave Radiation Absorption by Ilmenite Nanoparticles
Nanostructured radar absorbing materials (RAMs) have received steadily growing interest because of their fascinating properties and various applications compared with the bulk or micronized counterparts. These nanostructured materials have increased surface area, number of dangling bond atoms and unsaturated co -ordination on surface lead to interface polarization, multiple scatter and absorbin...
متن کاملMagnetic and microwave absorption properties of barium hexaferrite doped with La3+ and Gd3+
In this paper, BaLaxGdxFe12-2xO19 (x=0.2, 0.4, 0.6 and 0.8) were synthesized via sol-gel auto-combustion method. Fourier transform infrared spectroscopy (FTIR) of samples was represented that the bands at 400 and 500 cm-1 were related to the formation of hexaferrite phase. The (x-ray diffraction) XRD patterns were matched exactly with the structure of barium hexaferrite. (Field emission scanni...
متن کاملOne-pot reductive Amination of Carbonyl Compounds using NaBH4 and Fe3O4 Magnetic Nanoparticles
One-pot reaction of aldehydes or ketons with aniline derivatives was performed using NaBH4 and Fe3O4 magnetic nanoparticles (MNPs). The optimum amount of Fe3O4 MNPs was 5 mol% under solvent free condition. The corresponding products were obtained in good to excellent yields. The magnetically recoverable iron oxide nanoparticles are found to be efficient for synthesis of amine derivatives. These...
متن کامل