Study on Surface Permeability of Concrete under Immersion
نویسندگان
چکیده
In this paper, concrete specimens are immersed in ultrapure water, to study the evolutions of surface permeability, pore structure and paste microstructure following the prolonging of immersion period. According to the results, after 30-day immersion, the surface permeability of concrete becomes higher as compared with the value before immersion. However, further immersion makes the surface permeability decrease, so that the value measured after 150-day immersion is only half that measured after 30-day immersion. The early increase in surface permeability should be mainly attributed to the leaching of calcium hydroxide, while the later decrease to the refinement of pore structure due to hydration. The two effects work simultaneously and compete throughout the immersion period. The proposed mechanisms get support from microscopic measurements and observations.
منابع مشابه
Evaluation of Hybrid Fiber Reinforced Concrete Exposed to Severe Environmental Conditions
Hybrid fiber reinforced concrete (HFRC) consisting of two or more different types of fibers has been widely investigated because of its superior mechanical properties. In the present study, the effect of the addition of steel (0.25%, 0.5%, 0.75%, and 1% of concrete volume) and Polypropylene (0.2%, 0.4%, and 0.6% of concrete volume) fibers on the surface scaling resistance of concrete, depth of ...
متن کاملPermeation Properties and Pore Structure of Surface Layer of Fly Ash Concrete
This paper presents an experimental study on the nature of permeation properties and pore structure of concrete surface layers containing fly ash. Concretes containing different dosages of fly ash as a replacement for cement (15% and 30% by weight of total cement materials, respectively) were investigated. Concrete without any fly ash added was also employed as the reference specimen. Laborator...
متن کاملInfluence of Fly Ash on Surface Chloride Concentration Under Shallow Immersion Condition
In this paper, the influence of fly ash content on concrete surface chloride concentration was investigated through periodical tests of surface chloride concentration of concrete by immersing three kinds of concrete specimens in 5.0 wt.% sodium chloride solution. One kind of specimen is common concrete without fly ash, whereas the other two kinds of specimens are mixed with fly ash. The results...
متن کاملDetermination of Permeability of Concrete to Chloride Ions by Rapid Test Procedures
Methods which can be used to assess the chloride permeability of various types of concrete in a relatively short time are described. An electrical potential from 60-80 volt DC is applied either between a chloride solution ponded on a slab surface and the top of rebar mat, or between two faces at a core taken from a structure. The amount of chloride and sum of the electrical current which passes...
متن کاملEstimating an appropriate plastic concrete mixing design for cutoff walls to control leakage under the earth dam.
Making use of concrete materials in cut-off walls, because of their low permeability and standing high Hydraulic Gradient caused by underground drainage, has attracted great amount of attention. Using ordinary concrete with high elasticity modulus, compared to other materials may accompany with problems including brittleness of cutoffs due to dynamic stresses. To solve this problem, adding a ce...
متن کامل