Fabrication of low-temperature solid oxide fuel cells with a nanothin protective layer by atomic layer deposition
نویسندگان
چکیده
Anode aluminum oxide-supported thin-film fuel cells having a sub-500-nm-thick bilayered electrolyte comprising a gadolinium-doped ceria (GDC) layer and an yttria-stabilized zirconia (YSZ) layer were fabricated and electrochemically characterized in order to investigate the effect of the YSZ protective layer. The highly dense and thin YSZ layer acted as a blockage against electron and oxygen permeation between the anode and GDC electrolyte. Dense GDC and YSZ thin films were fabricated using radio frequency sputtering and atomic layer deposition techniques, respectively. The resulting bilayered thin-film fuel cell generated a significantly higher open circuit voltage of approximately 1.07 V compared with a thin-film fuel cell with a single-layered GDC electrolyte (approximately 0.3 V).
منابع مشابه
The study of Oxidation Behavior of AISI 439 Steel at the Presence of Manganese Oxides for the Application in Solid Oxide Fuel Cells
Long–term stability and oxidation resistance of AISI 439 ferritic stainless steel used as interconnects in solid oxide fuel cells can be improved by use of a protective coating. In this study the pack cementation method was employed to coat AISI 439 ferritic stainless steel with manganese. Isothermal oxidation was conducted at 800 ºC for 200 hours in static air to investigate the role of coatin...
متن کاملEffect of Seed Layer on the Morphology of Zinc Oxide Nanorods as an Electron Transport Layer in Polymer Solar Cells
Zinc oxide has been considered as a promising semiconductor material for fabrication of transparent conductive oxides (TCOs), electronic devices, optoelectronics, and solar cells. Among the various morphologies of zinc oxide, nanorods are more widely used because of the ease of synthesis and providing a direct path for the transport of charge carriers. The electrochemical deposi...
متن کاملInfluence of electroplating parameters on microstructure and amount of ceramic particle deposition in Ni-Co-CeO2-ZrO2 composite coating
Austenitic stainless steels are high performance steels that have various applications in solid oxide fuel cells and boiler tubes under high temperature operating conditions. The Cr2O3 oxide layer formed on the steel surface becomes unstable at high temperatures and reduces the oxidation resistance of the steel. Therefore, protection of these steels at high temperatures is essential. Therefore,...
متن کاملFabrication Of Cu(In,Ga)Se2 Solar Cells With In2S3 Buffer Layer By Two Stage Process
Cu(In,Ga)Se2 thin films (CIGS) on metallic substrate (titanium, molybdenum, aluminum, stainless steel) were prepared by a two-step selenization of Co-evaporated metallic precursors in Se-containing environment under N2 gas flow. Structural properties of prepared thin film were studied. To characterize the optical quality and intrinsic defect nature low-temperature photoluminescence, were perfor...
متن کاملElectrophoretic deposition of MnCr2O4 coating for solid oxide fuel cell metallic interconnects
In the present study, Mn - Cr spinel powder was synthesized through a solid state reaction. In the next step, the electrophoretic deposition (EPD) method was used to apply the MnCr2O4 spinel, as an oxidation-resistant layer, on SUS 430 stainless steel in a potential of 300 V/cm. The coated and uncoated samples were then pre-sintered in air at 900 °C for 3 h followed by cyclic oxidation at 800 °...
متن کامل