Effect of water absorption on the mechanical properties of hemp fibre reinforced unsaturated polyester composites
نویسنده
چکیده
Hemp fibre reinforced unsaturated polyester composites (HFRUPE) were subjected to water immersion tests in order to study the effects of water absorption on the mechanical properties. HFRUPE composites specimens containing 0, 0.10, 0.15, 0.21 and 0.26 fibre volume fraction were prepared. Water absorption tests were conducted by immersing specimens in a de-ionised water bath at 25 C and 100 C for different time durations. The tensile and flexural properties of water immersed specimens subjected to both aging conditions were evaluated and compared alongside dry composite specimens. The percentage of moisture uptake increased as the fibre volume fraction increased due to the high cellulose content. The tensile and flexural properties of HFRUPE specimens were found to decrease with increase in percentage moisture uptake. Moisture induced degradation of composite samples was significant at elevated temperature. The water absorption pattern of these composites at room temperature was found to follow Fickian behaviour, whereas at elevated temperatures it exhibited non-Fickian. 2006 Elsevier Ltd. All rights reserved.
منابع مشابه
Mechanical Properties and Water Absorption of Hemp Fibers–Reinforced Unsaturated Polyester Composites: Effect of Fiber Surface Treatment with a Heterofunctional Monomer
Hemp fibers–reinforced unsaturated polyester (UP) composites were prepared by hand lay-out compression molding. Hemp fibers were treated with isocyanatoethyl methacrylate (IEM), using dibutyltin dilaurate as a catalyst. The results indicated that fiber treatment significantly increased tensile strength, flexural strength, flexural modulus, and water resistance of the resulting composites, and y...
متن کاملThe Effect of Surface treatment on the Properties of Woven Banana Fabric based Unsaturated Polyester Resin Composites
The aim of this paper is to study the effect of silane treatment on woven banana fabric based unsaturated polyester resin composites. The fabric was treated with vinyl triethoxysilane. Woven banana fabric (WBF) reinforced unsaturated polyester resin (UPR) composites were fabricated by hand lay-up technique. The fabric content in the composite was kept constant to 35 %. The variation in the mech...
متن کاملProperties of Hemp Fibre Reinforced Concrete Composites
This research is concerned with the mechanical and physical properties of hemp fibre reinforced concrete (HFRC). An experimental program was developed based on the statistical method of fractional factors design. The variables for the experimental study were: 1) mixing method; 2) fibre content by weight; 3) aggregate size; and 4) fibre length. Their effects on the compressive and flexural perfo...
متن کاملEffect of Redmud Particulates on Mechanical Properties of BFRP Composites (TECHNICAL NOTE)
This article reports the effective usage of redmud(RM) an industrial waste ,as a novel filler in polymer matrix. The composite has been fabricated with redmud as secondary reinforcement in banana fiber reinforced polyester (BFRP) using compression molding technique. The mechanical properties such as tensile, flexural and impact strength have been studied for different fiber weight percentage, ...
متن کاملMechanical and Impact Properties of Untreated Jute Fabric Reinforced Polyester Laminates Compared with Different E- Glass Fibre Reinforced Laminates
In recent years, the improvement of properties of natural fibre reinforced laminates over the pure polymeric matrix has been thoroughly investigated with the aim of providing a possible replacement of E-glass fibre reinforced composites for some large-volume applications. In the present study, the properties of a jute/polyester laminate are compared with those yielded by two E-glass fibre woven...