Sputter-prepared (001) BiFeO3 thin films with ferromagnetic L10-FePt(001) electrode on glass substrates
نویسندگان
چکیده
Highly textured BiFeO3(001) films were formed on L10-FePt(001) bottom electrodes on glass substrates by sputtering at reduced temperature of 400°C. Good electric polarization 2Pr = 80 and 95 μC/cm2, comparable to that of the reported epitaxial films, and coercivity Ec = 415 and 435 kV/cm are achieved in the samples with 20-nm- and 30-nm-thick electrodes. The BiFeO3(001) films show different degrees of compressive strain. The relation between the variations of strain and 2Pr suggests that the enhancement of 2Pr resulted from the strain-induced rotation of spontaneous polarization. The presented results open possibilities for the applications based on electric-magnetic interactions.
منابع مشابه
The role of SrRuO3 bottom layer in strain relaxation of BiFeO3 thin films deposited on lattice mismatched substrates
Articles you may be interested in Role of defects in BiFeO3 multiferroic films and their local electronic structure by x-ray absorption spectroscopy High symmetric SrRuO3 (001) thin films: Perfectly lattice-matched electrodes for multiferroic BiFeO3
متن کاملL 10 ordering and microstructure of FePt thin films with Cu , Ag , and Au additive
The influence of Cu, Ag, and Au additives on the L10 ordering, texture, and grain size of FePt thin films has been examined. Lattice parameter data indicated that Au and Ag additives tended to segregate from FePt, but Cu alloyed with FePt. FePt films with Au or Ag additive showed 1–2 kOe higher coercivity values compared to a pure FePt film after annealing at 450 °C and above for 10 min. The ad...
متن کاملFerroelectric domain structures of epitaxial „001... BiFeO3 thin films
Ferroelectric domain structures of epitaxial BiFeO3 thin films on miscut 001 SrTiO3 substrates have been studied by transmission electron microscopy. BiFeO3 on 0.8° miscut substrates are composed of both 109° and 71° domains; in contrast, only 71° stripe domains are observed in BiFeO3 on 4° miscut 001 SrTiO3 substrates. The domain width in BiFeO3 on 4° miscut substrates increases as film thickn...
متن کاملOrientation of FePt nanoparticles on top of a-SiO2/Si(001), MgO(001) and sapphire(0001): effect of thermal treatments and influence of substrate and particle size
Texture formation and epitaxy of thin metal films and oriented growth of nanoparticles (NPs) on single crystal supports are of general interest for improved physical and chemical properties especially of anisotropic materials. In the case of FePt, the main focus lies on its highly anisotropic magnetic behavior and its catalytic activity, both due to the chemically ordered face-centered tetragon...
متن کاملDEPOSITION AND CHARACTERIZATION OF MULTIFERROIC BiFeO3 THIN FILMS
Title of Dissertation: DEPOSITION AND CHARACTERIZATION OF MULTIFERROIC BiFeO3 THIN FILMS Junling Wang, Doctor of Philosophy, 2005 Dissertation Directed By: Professor Manfred Wuttig, Department of Materials Science and Engineering Multiferroics, defined as materials with coexistence of at least two of the electric, elastic, and magnetic orders, have attracted enormous research activities recentl...
متن کامل