An in situ Study of NiTi Powder Sintering Using Neutron Diffraction

نویسندگان

  • Gang Chen
  • Peng Cao
  • Hugo F. Lopez
چکیده

This study investigates phase transformation and mechanical properties of porous NiTi alloys using two different powder compacts (i.e., Ni/Ti and Ni/TiH2) by a conventional press-and-sinter means. The compacted powder mixtures were sintered in vacuum at a final temperature of 1373 K. The phase evolution was performed by in situ neutron diffraction upon sintering and cooling. The predominant phase identified in all the produced porous NiTi alloys after being sintered at 1373 K is B2 NiTi phase with the presence of other minor phases. It is found that dehydrogenation of TiH2 significantly affects the sintering behavior and resultant microstructure. In comparison to the Ni/Ti compact, dehydrogenation occurring in the Ni/TiH2 compact leads to less densification, yet higher chemical homogenization, after high temperature sintering but not in the case of low temperature sintering. Moreover, there is a direct evidence of the eutectoid decomposition of NiTi at ca. 847 and 823 K for Ni/Ti and Ni/TiH2, respectively, during furnace cooling. The static and cyclic stress-strain behaviors of the porous NiTi alloys made from the Ni/Ti and Ni/TiH2 compacts were also investigated. As compared with the Ni/Ti sintered samples, OPEN ACCESS

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Processing of NiTi Foams by Transient Liquid Phase Sintering

Porous NiTi was produced by sintering pre-alloyed NiTi powders (with small Ni addition to form Ni-rich composition) with NaCl powders which are removed to create 40-60 vol.% macropores which are open to the surface, blocky in shape, and 100-400 lm in size. The microporosity present between the NiTi powders is infiltrated by an in situ created NiTi-Nb eutectic liquid which, after solidification,...

متن کامل

An in Situ Neutron Diffraction Mechanical Study of Superelastic Niti and Niti-tic Composites

Superelastic NiTi and NiTi-TiC composites were subjected to static uniaxial compressive loading while neutron diffraction spectra were simultaneously acquired. A methodology was established to obtain quantitative strain, texture and phase volume fraction information during the forward and reverse stress-induced martensitic transformation. Despite the presence of 10 vol. % of stiff TiC particles...

متن کامل

Porous NiTi alloy prepared from elemental powder sintering

An elemental powder sintering (EPS) technique has been developed for the synthesis of porous NiTi alloy, in which Ni and Ti powders are used as the reactants and TiH2 powder is added as a pore-forming agent and active agent. Effects of various experimental parameters (sintering temperature, sintering time, and TiH2 content) on the porosity, pore size and pore distribution as well as phase compo...

متن کامل

Mechanical Properties of Superelastic and Shape - Memory NiTi and NiTi - TiC Composites

The objective of this work was to study materials subjected to external loading where alternative deformation mechanisms are available to generate strains. In the case of shapememory and superelastic NiTi, these mechanisms are twinning and stress-induced phase transformation, respectively. Superelastic NiTi (51.0 at.% Ni) reinforced with 0, 10 and 20 vol.% TiC particles was fabricated by Hot Is...

متن کامل

IN SITU FABRICATION OF Al 2024-Mg2Si COMPOSITE BY SPARK PLASMA SINTERING OF REACTIVE MECHANICALLY ALLOYED POWDER

In situ Al2024- Mg2Si composite was fabricated by spark plasma sintering (SPS) of reactive powder. Reactive powder was obtained from mechanical alloying (MA) of elemental powders. Clad layers of in situ composite were fabricated on Al substrates by spark plasma sintering (SPS). Structural evolution during MA process and after SPS was investigated by X-ray diffractometery (XRD). Scanning electro...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2015