In situ investigations of structure-activity relationships of a Cu/ZrO2 catalyst for the steam reforming of methanol

نویسندگان

  • A. Szizybalski
  • F. Girgsdies
  • A. Rabis
  • Y. Wang
  • M. Niederberger
  • T. Ressler
چکیده

Structure-activity relationships of a nanostructured Cu/ZrO2 catalyst for the steam reforming of methanol (MSR) were investigated under reaction conditions by in situ X-ray absorption spectroscopy (XAS) and X-ray diffraction (XRD) combined with on-line mass spectrometry (MS). Temperature programmed activation by reduction in hydrogen or by reduction in a mixture of methanol and water (feed) was studied by time-resolved Cu K edge XANES and TG/DSC/MS measurements. Small and disordered CuO particles were identified as the main copper phase present in the precursors. After extended time on stream and treatment at 673 K in hydrogen, no significant sintering of the copper particles or deactivation of the reduced Cu/ZrO2 catalysts was detected indicating a superior stability of the material. The initially low steam reforming activity of the Cu/ZrO2 catalyst after reduction in hydrogen could be significantly increased by a temporary addition of oxygen to the feed. This increased activity after oxidative treatment is correlated to an increasing amount of oxygen in the copper particles. Cu NMR studies detected only a minor degree of microstrain in the active copper phase of the Cu/ZrO2 catalyst. The decreased reducibility of CuO/ZrO2, the low degree of microstrain, and the correlation between the amount of oxygen remaining in the copper particles and the catalytic activity indicate a different metal support interaction compared to Cu/ZnO catalysts.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Methanol steam reforming; Effects of various metal oxides on the properties of a Cu-based catalyst

Ternary Cu/ZnO/metal oxide catalysts are prepared through the co-precipitation method under strict control of parameters like pH, calcination conditions, and precipitation temperature in a systematic manner. The metal oxides applied in this study consist of Al2O3, ZrO2, La2O3 and Ce2O3. The distinction of this work in comparison with similar research is a comprehensive investigatation of the ca...

متن کامل

Methanol Steam Reforming Catalyzing over Cu/Zn/Fe Mixed Oxide Catalysts

Methanol steam reforming plays a pivotal role to produce hydrogen for fuel cell systems in a low temperature range. To accomplish higher methanol conversion and lower CO production, the reaction was catalyzed by CuZnFe mixed oxides. Various ratios of Fe and Cu/Zn were coprecipitated in differential method to optimize the CuZnFe structure. The sample containing 45Cu50Zn5Fe (Wt. %) revealed its m...

متن کامل

Cyclic Regeneration of Cu/ZnO/Al2O3 Nano Crystalline Catalyst of Methanol Steam Reforming for Hydrogen Production in a Micro-Fixed-Bed Reactor

Hydrogen can be produced for fuel cell applications by using methanol steam reforming reaction. In this article, a method was developed for regeneration of accelerated deactivated methanol-steam-reforming catalyst. Successive deactivation–regeneration cycles were studied in a 250 hours test for the first time including 6 regeneration cycles. It is shown that regeneration of the catalyst in ...

متن کامل

Effect of Pt on Zn-Free Cu-Al Catalysts for Methanol Steam Reforming to Produce Hydrogen

Steam reforming of methanol can be considered as an attractive reaction aiming at hydrogen production for PEM fuel cells. Although Cu/Al-contained catalysts are considerably evaluated in this reaction, further evaluation is essential to evaluate the impact of some promoters like Pt in order to find a comprehensively optimized catalyst. Pt promoter is employed with different methods in this ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2006