Fatigue behavior of Austenitic Type 316L Stainless Steel
نویسندگان
چکیده
The aim of this work is to determine the fatigue life of 316L stainless steel. The mechanisms of fatigue of 316L stainless steels were investigated and discussed. The fatigue tests were carried out at constant-amplitude cyclic loading with load ratio R=0.1. Scanning Electron Microscope (SEM) is then used to examine the fracture surface. The results show that the fatigue limit of 316L stainless steel was 146.45 MPa.
منابع مشابه
An investigation on the passivation behavior of nitrogen enriched AISI 316L austenitic stainless steel
In the present work the effects of plasma nitridization on the passivation behavior of AISI 316L was investigated. To do this; nitriding treatments were carried out at 420°C for 1, 2, 4 and 16 hours. The phase composition and structure of the nitrided layer were studied by Low Angle X-ray diffraction and Scanning Electron Microscopy. The hardness of samples also was evaluated by Vickers microha...
متن کاملThe combined effect of molybdenum and nitrogen on the fatigued microstructure of 316 type austenitic stainless steel
Introduction The mechanical properties of austenitic stainless steels, including the low cyclic fatigue behavior have been a subject of numerous studies [1-8]. Nitrogen addition, in general, increases the fatigue strength by decreasing the stacking fault energy of austenitic stainless steels [6]. The stacking fault energy has a strong influence on the cross slip difficulty, thus it affects the ...
متن کاملBiological behaviour of human umbilical artery smooth muscle cell grown on nickel-free and nickel-containing stainless steel for stent implantation
To evaluate the clinical potential of high nitrogen nickel-free austenitic stainless steel (HNNF SS), we have compared the cellular and molecular responses of human umbilical artery smooth muscle cells (HUASMCs) to HNNF SS and 316L SS (nickel-containing austenitic 316L stainless steel). CCK-8 analysis and flow cytometric analysis were used to assess the cellular responses (proliferation, apopto...
متن کاملEffect of Relative Humidity in High Temperature Oxidation of Ceria Nanoparticles Coating on 316L Austenitic Stainless Steel
............................................................................................................................ ii TABLE OF CONTENTS ....................................................................................................... iv LIST OF FIGURES ................................................................................................................ vi LIST OF TABL...
متن کاملEffect of plastic deformation on anelastic mechanical losses in multicomponent substitutional austenitic alloys
Complex two-component peak of anelastic mechanical losses was observed in multicomponent substitutional austenitic alloys after prior plastic deformation. In AISI 316L, AISI 316LN, AISI 310 and AISI 304 austenitic stainless steels, this peak is situated in the wide range of temperature from 200 to 400K. Characteristics of the observed peak for different thermo-mechanical treatments were studied...
متن کامل