Structural Investigation of Chemical Treated Polyester Fibers Using Saxs and Other Techniques
نویسنده
چکیده
Structural macromolecular parameters of normal and treated (acid & alkali) polyester fibers have been investigated using Small Angle X-ray Scattering (SAXS) technique. Average diameters were calculated from Scanning electron microscope (SEM) micrographs and mechanical parameters were estimated using Instron. Further, crystallinity parameters of the same fibers have been determined using X-ray diffraction (XRD) and Thermal analysis. These results supplement the findings of SAXS, SEM and Instron. Comparison and analysis of results confirm some changes in the microstructure of fiber after chemical treatment due to breaking of macromolecules. The findings conclude that degradation of acid treated fiber is more than that of alkali treated fiber.
منابع مشابه
Comparison of dyeing of polyester fibers with natural dye and bio-mordant
In this study, dyeing of two regenerated polyester fibers, poly-trimethylene terephthalate (PTT) and poly-lactic acid (PLA), with natural dyes were compared with that of poly-ethylene terephthalate (PET) fiber. Lac was used as the primary natural colorant while Catechu was chosen as a natural color that can also act as a biomordant. The effects of temperature, initial pH of dye bath and dyeing ...
متن کاملNaphthalene-based azo dyes: Synthesis, characterization and dyeing performance on polyester fibers
In the present study, five naphthalene-based azo dyes were obtained using classical azo coupling reactions. The structure of the dyes was characterized and confirmed by the UV-vis, FT-IR, 1H NMR and 13C NMR analyses. The solvatochromic behavior of the dyes was studied in a set of 10 solvents with different polarity and considerable results were obtained. The dyes were applied as disperse dyes t...
متن کاملInvestigation on magnetic and microwave behavior of magnetite nanoparticles coated carbon fibers composite
Radar absorbing materials, i.e. magnetite (Fe3O4) coated carbon fibers (MCCFs) were fabricated by electro-deposition technique. Black-colored single spinel phase Fe3O4 nanoparticles was easily synthesized by hydrothermal method using reduction of a Fe (III) - Triethanolamine complex in an aqueous alkaline solution at 60-80 ◦C. Uniform and compact Fe3O4 films were fabricated on nitric acid treat...
متن کاملInvestigation of Mechanical Properties of Lithium-Based Geopolymer Composites Reinforced with Basalt Fibers
Recently, geopolymer binders have been considered because of low cost, simple processes for synthesis and many raw materials in nature. Geopolymer with brittle nature does not have high strength and cannot be used alone for structural materials. Therefore, to use in different structures, the composite which is reinforced with fibers such as carbon, glass, basalt, etchasbeen used. In this resear...
متن کامل