Remineralization effects of xylitol on demineralized enamel.
نویسندگان
چکیده
We morphologically determined the effects of xylitol on the remineralization of artificially demineralized enamel. The samples were demineralized and then immersed in a remineralizing solution with or without 20% xylitol at 37 degrees C for 2 weeks. Samples were observed using contact microradiography, a multipurpose image processor (MIP) and a high-resolution electron microscope (HRTEM). Contact microradiography indicated that remineralization occurred in the surface and deep layers of samples immersed in a non-xylitol solution. Samples immersed in a xylitol solution demonstrated less mineralization in the outer 10 microm of the outermost surface layers, but more mineralization in the middle and deep layers, than was observed in the non-xylitol samples. The MIP evaluation indicated that remineralization was more prominent in layers at depths of 50-60 microm in the xylitol samples than in the non-xylitol samples. Observation of the xylitol samples by HRTEM revealed crystals of various sizes and irregular shapes with unclear crystal angles in the outermost surface layers. In the middle layers, they had thickened and angles of crystals are clear. These results indicate that xylitol can induce remineralization of deeper layers of demineralized enamel by facilitating Ca2+ movement and accessibility.
منابع مشابه
Effect of chewing gums with xylitol, sorbitol and xylitol-sorbitol on the remineralization and hardness of initial enamel lesions in situ
BACKGROUND The purpose of this study was to determine the effect of three chewing gums and paraffin on the remineralization and the hardness of demineralized enamel. MATERIALS AND METHODS A total of 12 subjects wore intraoral palatal appliances with two demineralized bovine enamel slabs. The study consisted of four experimental periods each lasting 21-days, during which subjects were assigned...
متن کاملRemineralization of Enamel Subsurface Lesions
The aim of the present study was to determine the remineralization effects of xylitol chewing gum containing funoran and calcium hydrogenphosphate on enamel subsurface lesions in humans. The study was a double-blind, randomized, cross-over design, with 4 types of gum: (1) xylitol gum, (2) xylitol gum containing funoran and calcium hydrogenphosphate, (3) sugar gum, and (4) gum base as a control....
متن کاملComparison Study on Casein Phosphopeptide-Amorphous Calcium Phosphate Paste and Fluoride Gel on Remineralization of Demineralized Enamel Lesions
Objective: Tooth surface undergoes continuous remineralization and demineralization. The aim of this study was to compare the effect of Caseinphosphopeptide-amorphous calcium phosphate (CPP-ACP) paste and Fluoride gel on the microhardness of demineralized enamel lesions. Methods: Frothy eight specimens of premolar teeth were chosen and randomly divided to 4 groups of 12. After the initial m...
متن کاملEffects of experimental xylitol varnishes and solutions on bovine enamel erosion in vitro.
This in vitro study aimed to analyze the effects of application of xylitol varnishes and solutions to protect against enamel erosion. Twelve bovine enamel specimens were pre-treated with 5% NaF-Duraphat varnish, 10% xylitol varnish, 20% xylitol varnish, placebo varnish, 5% NaF solution, 10% xylitol solution or 20% xylitol solution. The varnishes and solutions were applied for 6 h and 1 min, res...
متن کاملEffect of a xylitol and fluoride containing toothpaste on the remineralization of human enamel in vitro.
The aim of this study was to examine the effect of a fluoride and xylitol containing toothpaste on the remineralization of human enamel using Quantitative Light-induced Fluorescence (QLF). Human extracted teeth were cut longitudinally into three or four parts, and artificial subsurface lesion windows (2 mm x 3 mm) were created by immersion in demineralizing solution. Each enamel sample (n = 7) ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Journal of electron microscopy
دوره 52 5 شماره
صفحات -
تاریخ انتشار 2003