The photoluminescence properties of Eu2+-activated α’-Sr2SiO4 and α’-Ba2SiO4 with a high Eu2+ concentration were investigated. In the case of Sr2−xEuxSiO4, emission was shifted from 585 to 611 nm with increasing the total Eu2+ concentration (x) from 0.1 to 0.8. This trend was similar to that in Ba2−xEuxSiO4, where the emission was shifted from 513 to 545 nm. The large redshifts in both the excitation and emission spectra were discussed in terms of the Eu2+ occupancies on two kinds of M sites and their local structural changes (M: Sr and Ba).
منابع مشابه
Nanosized strontium aluminate phosphors prepared via a reverse microemulsion route
Nanosized strontium aluminate phosphors co-activated by Eu2+ and Dy3+ were prepared via a novel reverse microemulsion process. This new ynthesis technique lowered the synthesis temperature of SrAl2O4: Eu2+, Dy3+ phosphors to as low as 900 ◦C, and also reduced the particle size o the nanometer scale (around 40 nm). In the microemulsion process, the constituent cations were trapped by numerous na...
متن کاملCorrelation of Structure, Tunable Colors, and Lifetimes of (Sr, Ca, Ba)Al2O4:Eu2+, Dy3+ Phosphors
(Sr, Ca, Ba)Al₂O₄:Eu2+, Dy3+ phosphors were prepared via a high temperature solid-state reaction method. The correlation of phase structure, optical properties and lifetimes of the phosphors are investigated in this work. For the (Sr, Ca)Al₂O₄:Eu2+,Dy3+ phosphors, the different phase formation from monoclinic SrAl₂O₄ phase to hexagonal SrAl₂O₄ phase to monoclinic CaAl₂O₄ phase was observed when...
متن کاملLuminescent Properties of Sr4Si3O8Cl4:Eu2+, Bi3+ Phosphors for Near UV InGaN-Based Light-Emitting-Diodes
Sr4Si3O8Cl4 co-doped with Eu2+, Bi3+ were prepared by the high temperature reaction. The structure and luminescent properties of Sr4Si3O8Cl4:Eu2+, Bi3+ were investigated. With the introduction of Bi3+, luminescent properties of these phosphors have been optimized. Compared with Sr3.90Si3O8Cl4:0.10Eu2+, the blue-green phosphor Sr3.50Si3O8Cl4:0.10Eu2+, 0.40Bi3+ shows stronger blue-green emission ...
متن کاملEffect of Composition and Impurities on the Phosphorescence of Green-Emitting Alkaline Earth Aluminate Phosphor
Recent improvements to SrAl2O4:Eu2+, Dy3+ phosphors have enabled the use of luminescent hosts with a stable crystal structure and high physical and chemical stability, thus overcoming the bottleneck in the applicability of ZnS:Cu phosphors. However, enhancement of afterglow lifetime and brightness in SrAl2O4:Eu2+, Dy3+ phosphors remains a challenging task. Here, we have improved the afterglow c...
متن کاملThe Enhanced Red Emission and Improved Thermal Stability of CaAlSiN3:Eu2+ Phosphors by Using Nano-EuB6 as Raw Material
Synthesizing phosphors with high performance is still a necessary work for phosphor-converted white light-emitting diodes (W-LEDs). In this paper, three series of CaAlSiN₃:Eu2+ (denoted as CASN:Eu2+) phosphors using Eu₂O₃, EuN and EuB₆ as raw materials respectively are fabricated by under the alloy precursor normal pressure nitridation synthesis condition. We demonstrate that CASN:Eu2+ using na...
متن کامل