New synthesis of a porous Si/TiO2 photocatalyst: testing its efficiency and stability under visible light irradiation.
نویسندگان
چکیده
TiO(2) nanoparticles were directly coupled with porous silicon and this novel composite material shows very strong photocatalytic activity for the degradation of Rhodamine B with high photochemical stability under visible light irradiation.
منابع مشابه
Synthesis, Characterization, and Efficiency Testing of Ag3PO4/TiO2 Heterogeneous Nano-Photocatalyst in Removing Gaseous Formaldehyde as an Occupational Carcinogen
Introduction: Rapid population growth and industrialization have increased chemical pollutants. Some studies show that employee exposure to formaldehyde in industrial places, hospitals, and laboratory settings is more than the allowed limits. Therefore, it is necessary to implement a proper control system to reduce this exposure. This study aimed to synthesize Ag3PO4/TiO2 nanocomposite, determi...
متن کاملSynthesis of nanocomposite based on Semnan natural zeolite for photocatalytic degradation of tetracycline under visible light
This study investigated the photocatalytic behaviors for the nanocomposite of TiO2 P25 and Semnan natural zeolite in the decomposition of tetracycline under visible light in an aqueous solution. The structural features of the composite were investigated by a series of complementary techniques that included X-ray diffractometer (XRD), Fourier transform infrared spectroscopy (FTIR), scanning elec...
متن کاملPhotocatalytic degradation of methyl orange using TiO2:Mg2+/zeolite composite under visible light irradiation
Photodegradation of methyl orange was investigated using synthesized TiO2:Mg2+/zeolite as the photocatalyst. The photocatalyst was characterized by X-ray, XRF, FT-IR, and SEM. The photocatalytic activities of TiO2:Mg2+/zeolite samples were evaluated in the degradation of methyl orange under visible light irradiation. The appropriate content of Mg in the composite was obtained as 4.711 wt% with ...
متن کاملSynthesis, Characterization, and Application of Zr,Ce-TiO2/SiO2 Nanocomposite Thin Film as Visible-light Active Photocatalyst
A novel Zr,Ce-TiO2/SiO2 nanocomposite thin film was successfully prepared with various amounts of Zr4+ and Ce4+ as codopant ions for self-cleaning applications. A thin film was coated on a tile substrate by dip-coating and porous Zr,Ce-TiO2/SiO2 was obtained after heat treatment for 2 hours at 500 °C. The SEM images an...
متن کاملVISIBLE-LIGHT-ACTIVE NITROGEN DOPED TIO2 NANOPARTICLES PREPARED BY SOL-GEL ACID CATALYZED REACTION
Yellow-colored nitrogen doped TiO2 photocatalyst and a pure TiO2 powder were synthesized via sol-gel method using TiCl4 and urea as raw materials. However, the synthesis procedure for nitrogen doped TiO2 was catalyzed by acid that dialed with controlled precipitation and slow nucleation. According to XRD analysis, the nitrogen doped TiO2 consisted of anatase phase of titania which was a signifi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Photochemical & photobiological sciences : Official journal of the European Photochemistry Association and the European Society for Photobiology
دوره 5 7 شماره
صفحات -
تاریخ انتشار 2006