Effect of age and chemical treatments on characteristic parameters for active and porous sublayers of polymeric composite membranes.

Changes in the transport parameters and the chemical nature of the surface of composite polyamide/polysulfone membranes due to both aging and treatment with chemical products (HCl, H(3)NO, and NaOH) have been considered. Hydraulic and salt permeability were obtained from water flow and salt diffusion measurements, respectively, and their values seem to indicate a modification in the structural parameters (porosity/thickness) of aging samples, while HCl and HNO(3) treatments will act in the opposite way. Chemical modifications in the membrane surfaces were studied by X-ray photoelectron spectroscopy (XPS), which mainly show the effect of H(3)NO and HCl on the polyamide active layer of the membranes (polyamide oxidation), but no chemical damage for that sublayer. Electrical characterization of both sublayers of the composite membranes were determined from impedance spectroscopy (IS) measurements using equivalent circuits as models, and these results indicate: (i) a strong increase of the membrane electrical resistance as a consequence of aging, mainly that associated with the active sublayer (30 times higher for an old sample than for a fresh one) and treatment with NaOH; (ii) the reduction of this effect when the samples were treated with HCl and HNO(3) solutions. Changes in the values of the electrical resistance of the composite membranes are in agreement with those obtained for permeabilities, but the electrical parameter also allows the determination of the contribution of each sublayer.