Influence of radiopaque fillers on physicochemical properties of a model epoxy resin-based root canal sealer
نویسندگان
چکیده
OBJECTIVE To verify the influence of radiopaque fillers on an epoxy resin-based sealer. MATERIAL AND METHODS Experimental sealers were formulated by adding 20%, 40%, 60%, 80%, 100% and 120% of calcium tungstate, ytterbium trifluoride or barium sulphate by weight to an epoxy-resin-base. Setting time, flow, film thickness, radiopacity, sorption, solubility, pH and push-out bond strength were evaluated. RESULTS The setting time ranged from 373 to 612.66 min, the flow varied from 13.81±0.49 to 22.49±0.37 mm, and the film thickness ranged from 16.67±5.77 to 33.33±11.54 µm. The lowest pH was 5.47±0.53, and the highest was 6.99±0.03. Radiopacity varied from 0.38±0.04 to 2.57±0.21 mmAl and increased with the amount of filler. Calcium tungstate sealers had a higher sorption and solubility than other sealers. There was no significant difference in the push-out bond strength among the fillers at the 120% concentration. CONCLUSION The inorganic fillers evaluated and their concentrations affect the physicochemical properties of an epoxy resin-based root canal sealer.
منابع مشابه
The antibacterial activity of an epoxy resin-based dental sealer containing bioactive glass, hydroxyapatite, and fluorohydroxyapatite nanoparticles against Enterococcus Faecalis and Streptococcus mitis
Objective(s): The present study aimed to investigate the antibacterial properties of a conventional epoxy-based dental sealer modified with synthesized bioactive glass (BG), hydroxyapatite (HA), and fluorine-substituted hydroxyapatite (FHA) nano-fillers. Materials and Methods: The synthesized nano-fillers were incorporated into the conventional epoxy-based dental seaer at the concentratio...
متن کاملPhysicochemical Properties of Epoxy Resin-Based and Bioceramic-Based Root Canal Sealers
Three bioceramic sealers (EndoSequence BC sealer, EndoSeal MTA, and MTA Fillapex) and three epoxy resin-based sealers (AH-Plus, AD Seal, and Radic-Sealer) were tested to evaluate the physicochemical properties: flow, final setting time, radiopacity, dimensional stability, and pH change. The one-way ANOVA and Tukey's post hoc test were used to analyze the data (P = 0.05). The MTA Fillapex sealer...
متن کاملInfluence of root canal sealer on the radiographic appearance of filling voids in maxillary single-rooted teeth
OBJECTIVE This study compared the influence of three epoxy resin-based sealers with distinct radiopacities on the observers' ability to detect root canal filling voids during radiographic analysis. MATERIAL AND METHODS The root canals of 48 extracted maxillary canines were prepared and divided into three groups. Each group was laterally condensed with one sealer (AH Plus®, Acroseal® or a non-...
متن کاملInfluence of endodontic sealer composition and time of fiber post cementation on sealer adhesiveness to bovine root dentin.
This study aimed to assess the influence of the type of endodontic sealer (salicylate resin-based sealer vs. two endodontic sealers) and the time of fiber post cementation after root filling on the post adhesion to bovine root dentin. Sixty bovine roots were assigned to six groups (n=10), considering an experimental design with two factors (factorial 3x2): endodontic sealer factor in three leve...
متن کاملThe effect of a resin-based sealer cement on micropunch shear strength of dentin.
Dentinal tubules occupy a substantial proportion of total dentin volume, especially of inner dentin. Resin-based sealer cements are known to penetrate deeply into dentinal tubules, but their ability to influence root strength is controversial. In this study, the contribution of dentinal tubules to shear strength and the influence of a resin-based sealer on shear strength were evaluated. Coronal...
متن کامل