Study of Crystallization Process in V-substituted Finemet Alloys
نویسندگان
چکیده
Nanocrystalline soft magnetic alloys can be produced by partial crystallization of amorphous precursor. The aim of this paper was to study the influence of Nb substitution by vanadium (V) in Fe73.5Cu1Nb3-xVxB9Si13.5 (x=1.5, 3) alloys on their crystallization process and the glass forming ability because the growth of the α-Fe(Si) crystals is reduced by (Nb) diffusion barrier. Amorphous ribbons were prepared by melt-spinning technique. Crystallization process of amorphous alloys was examined by Different thermal analysis (DTA) in order to determine the crystallization temperatures and by X-ray powder diffraction measurements (XRD). Atomic pair correlation function G(r) and Radial distribution function R(r) has been calculated for better characterisation of as-quenched samples. It was found that higher V content accelerates crystallization process and causes worse glass forming ability. From DTA measurement was found decreasing of crystallization temperatures with higher V content.
منابع مشابه
Variation of Magnetization and Curie temperature with Isothermal Annealing of Higher Cr Content of Fe73.5-
This is well known that amorphous state is metastable. Metastability of amorphous or glassy metal alloys offers the possibility of phase separation diffusion of various species and structural relaxation even though the alloys remains amorphous when they are annealed at temperature well below the crystallization temperature. All these changes have effect on the intrinsic magnetic properties such...
متن کاملInvestigation on the crystallization mechanism difference between FINEMET® and NANOMET® type Fe-based soft magnetic amorphous alloys
متن کامل
Magnetic Properties and Crystallization Kinetics of a Mn-Doped FINEMET Precursor Amorphous Alloy
The kinetics of nanocrystallization of a Mn-doped FINEMET alloy from its amorphous precursor is reported. The alloy studied was of a composition (Fe1 Mn )73 5Nb3CuSi13 5B9 where = 0 05. X-ray diffraction (XRD) confirmed that -FeSi is the product of primary nanocrystallization. Crystallization kinetics were studied using time-dependent magnetization, ( ), as a measure of the volume fraction crys...
متن کاملMagnetic and structural properties and crystallization behavior of Si-rich FINEMET materials
The magnetic and structural properties of an Si-rich grade FINEMET alloy with a composition of Fe73.5Si16.1B6.4Nb2.9Cu1.1 in at% [Fe82.7Si9.1B1.4Nb5.4Cu1.4 (wt%)] were investigated after primary and secondary crystallization of ribbon samples. Optimally annealed ribbons exhibited a homogeneous microstructure composed of B7 nm DO3 nanocrystals surrounded by the retained amorphous phase. This is ...
متن کاملThe kinetics of nanocrystallization and microstructural observations in FINEMET, NANOPERM and HITPERM nanocomposite magnetic materials
This paper presents experimental observations of the nanocrystallization process in materials having Fe–Si (FINEMET), a-Fe (NANOPERM), and a0-FeCo (HITPERM) nanocrystals coupled through an amorphous phase. Crystallization kinetics and chemical partitioning during crystallization are described. Isothermal nanocrystallization is discussed in the framework of the Johnson–Mehl–Avrami–Kolmogorov mod...