Hardness evolution of AZ80 magnesium alloy processed by HPT at different temperatures
نویسندگان
چکیده
Discs of an extruded AZ80 magnesium alloy were processed by high-pressure torsion (HPT) using 6.0 GPa up to 10 turns at different temperatures (296 K and 473 K). The disc surfaces and cross-sectional planes were examined before and after processing using scanning electron microscopy (SEM) and Vickers microhardness (Hv). The microhardness results at the surface show differences in the strength of the material as a function of distance from the disc centres up to saturation, as well as a function of distance from the bottom to the surface in the cross-sectional plane. This study analyses the effect of processing temperature on the evolution of microhardness in the AZ80 magnesium alloy processed by high-pressure torsion. © 2017 Brazilian Metallurgical, Materials and Mining Association. Published by Elsevier Editora Ltda. This is an open access article under the CC BY-NC-ND license (http:// creativecommons.org/licenses/by-nc-nd/4.0/).
منابع مشابه
Examining the microhardness evolution and thermal stability of an Al–Mg–Sc alloy processed by high-pressure torsion at a high temperature
An Al–3% Mg–0.2% Sc alloy was solution treated and processed through 10 turns of highpressure torsion (HPT) at 450 K. Afterwards, the HPT-processed alloy was annealed for 1 h at temperatures ranging from 423 to 773 K and its mechanical properties and microstructural evolution were examined using microhardness measurements and electron backscattered diffraction (EBSD) analysis. The results demon...
متن کاملThermal stability and superplastic behaviour of an Al-Mg-Sc alloy processed by ECAP and HPT at different temperatures
An Al-3%Mg-0.2%Sc alloy was processed by ECAP and HPT at different temperatures. Afterwards, samples subjected to 10 turns of HPT at 300 and 450 K, 8 passes of ECAP at 300 K and 10 passes of ECAP at 600 K were annealed for 1 hour at 523 K and their mechanical properties and microstructure were examined using microhardness measurements and EBSD analysis. In addition, tensile specimens with simil...
متن کاملHardening and thermal stability of a nanocrystalline CoCrFeNiMnTi0.1 high-entropy alloy processed by high- pressure torsion
A CoCrFeNiMnTi0.1 high-entropy alloy (HEA) was subjected to high-pressure torsion (HPT) processing under 6.0 GPa pressure up to 10 turns. XRD results reveal that the initial and HPT-processed microstructures consist of a single fcc phase and there is no evidence for creating a new phase and the occurrence of a phase transformation during HPT processing. It is shown that there is a gradual evolu...
متن کاملHardening of an Al0.3CoCrFeNi high entropy alloy via high-pressure torsion and thermal annealing
High-pressure torsion (HPT) and thermal annealing were applied to a face-centered cubic as-cast Al0.3CoCrFeNi high entropy alloy. Processing by HPT produced a nanostructure with a higher incremental hardness than in most HPT single-phase materials and subsequent annealing at appropriate temperatures gave an ordered body-centered cubic secondary phase with an additional increase in hardness. The...
متن کاملEffect of Y Addition on the Semi-Solid Microstructure Evolution and the Coarsening Kinetics of SIMA AZ80 Magnesium Alloy
Semi-solid feedstock of AZ80 magnesium alloy modified by trace rare-earth Y element (0, 0.2, 0.4, 0.8 wt. %) was fabricated by strain-induced melting activation (SIMA) in the form of extrusion and partial remelting. The effect of Y addition on the microstructure evolution of the extruded and isothermally heat treated alloy was observed by using an optical microscope (OM), scanning electron micr...
متن کامل