Biaxial Yield Surface Investigation of Polymer-Matrix Composites
نویسندگان
چکیده
This article presents a numerical technique for computing the biaxial yield surface of polymer-matrix composites with a given microstructure. Generalized Method of Cells in combination with an Improved Bodner-Partom Viscoplastic model is used to compute the inelastic deformation. The validation of presented model is proved by a fiber Bragg gratings (FBGs) strain test system through uniaxial testing under two different strain rate conditions. On this basis, the manufacturing process thermal residual stress and strain rate effect on the biaxial yield surface of composites are considered. The results show that the effect of thermal residual stress on the biaxial yield response is closely dependent on loading conditions. Moreover, biaxial yield strength tends to increase with the increasing strain rate.
منابع مشابه
An Experimental Investigation on Fracture Analysis of Polymer Matrix Composite under Different Thermal Cycling Conditions
Fracture analysis of glass/epoxy composites under different thermal cycling conditions is considered. Temperature difference, stacking sequence, fiber volume fraction and number of thermal cycles are selected as the experimental design factors. The Taguchi method is implemented to design of the experiment and an apparatus is developed for automatic thermal cycling tests. The tensile tests are d...
متن کاملOpen-Hole Size and Thermal Cycling Effects on Mass Loss and Surface Degradation of Polymer Matrix Composites
Degradation is a common problem for polymer matrix composites (PMCs) under low thermal cycling conditions. This paper investigates the effects of low thermal cycling on total mass loss (TML) and surface degradation of PMCs. Unnotched and open-hole specimens were weighed before and after low thermal cycling. The total mass loss and surface degradation of the specimens were studied over 250 cycle...
متن کاملPREDICTING THE STIFFNESS OF BIAXIAL BRAIDED FIBER COMPOSITES BY INCORPORATION OF CARBON NANO FIBER
In this study, carbon nano fibers (CNFs) were mixed into epoxy resin through a magnetic stirrer and again mixed using ultra sonicator. Using hand layup technique, biaxial braided fiber composites were prepared with unfilled, 0.2, 0.5 and 1 wt% CNF. Tensile test and shear test was performed to identify the tensile strength and shear strength of the composites. Fractured surface of the tensile sp...
متن کاملSurface Degradation of Polymer Matrix Composites Under Different Low Thermal Cycling Conditions
The principal effects of mass degradation on polymer matrix composites (PMCs) are the decay of mechanical properties such as strength, elongation, and resilience. This degradation is a common problem of the PMCs under thermal cycling conditions. In this article, composite degradation was investigated by measurement of total mass loss (TML) using the Taguchi approach. Thermal cycling tests were ...
متن کاملInvestigation of Vacancy Defects on the Young’s Modulus of Carbon Nanotube Reinforced Composites in Axial Direction via a Multiscale Modeling Approach
In this article, the influence of various vacancy defects on the Young’s modulus of carbon nanotube (CNT) - reinforcement polymer composite in the axial direction is investigated via a structural model in ANSYS software. Their high strength can be affected by the presence of defects in the nanotubes used as reinforcements in practical nanocomposites. Molecular structural mechanics (MSM)/finite ...
متن کامل