Heat Curing of Soy Protein Films
نویسندگان
چکیده
Modification of soy protein film properties by heat-curing was studied. Glycerin-plasticized films were cast from alkaline aqueous solutions of soy protein isolate. Films were heated at 80 or 95°C for 2, 6, 14, or 24 h. Tensile strength (TS), elongation at break (E), moisture content (MC), water solubility (WS), water vapor permeability (WVP), and color of heated and control films were measured. Heated films had increased TS and -\-b (yellowness) Hunter color values and reduced £, MC, WS, and WVP values. These effects were enhanced as heating time and temperature increased.
منابع مشابه
Heat Curing of Soy Protein Films at Selected Temperatures and Pressures
Vacuum and temperature effects on moisture content, water vapor permeability (WVP), color (L, a, b, and DE), tensile strength (TS), elongation (E), and total soluble matter (TSM) of soy protein isolate (SPI) films were examined. SPI films were cured at 60, 72.5, or 85 °C and at 101.3, 81.32, or 61.32 kPa for 24 h. As a result of heat-curing moisture content, WVP, E, and TSM decreased, and total...
متن کاملPreparation and Characterization of Pullulan-Soy Protein Concentrate Biocomposite Film
The non-biodegradable nature of plastic packaging has brought about an attention in bio-basedpackaging materials. Edible composite films were prepared using soy protein concentrate (SPC) and pullulan(PUL) biopolymer at five different ratio (100:0; 70:30; 50:50; 30:70 and 0:100) with glycerol as plasticizer bycasting-evaporation method. The thickness, mechanical properties, water vapor permeabil...
متن کاملStable nano-sized emulsions produced from soy protein and soy polysaccharide complexes.
In this research, a simple, green and effective strategy was developed to produce long-term stable oil in water emulsion from soy protein and soy polysaccharide. Soy protein and soy polysaccharide formed dispersible complexes at pH around 3.25 aqueous solution through electrostatic and hydrophobic interactions. A high pressure homogenization produced the protein/polysaccharide complex emulsion ...
متن کاملPreparation and Characterization of All-Biomass Soy Protein Isolate-Based Films Enhanced by Epoxy Castor Oil Acid Sodium and Hydroxypropyl Cellulose
All-biomass soy protein-based films were prepared using soy protein isolate (SPI), glycerol, hydroxypropyl cellulose (HPC) and epoxy castor oil acid sodium (ECOS). The effect of the incorporated HPC and ECOS on the properties of the SPI film was investigated. The experimental results showed that the tensile strength of the resultant films increased from 2.84 MPa (control) to 4.04 MPa and the el...
متن کاملProperty Modification of Edible Wheat, Gluten-Based Films
Procedures were developed to produce edible wheat, gluten-based films. A film was produced as a standard. Five additional films were then produced by modifying the initial film-forming solution. Modifications included changing the plasticizer, partially substituting wheat gluten with soy protein isolate and corn zein, and incorporating two acetylated monoglyceride products. All films were chara...
متن کامل