Influence of Oxidation on Electrical Properties of Compacted Cu Nanopowders
نویسندگان
چکیده
The phase composition and electrical transport properties of Cu powder obtained by electric spark dispersion and the pellets manufactured from this powder were studied by X-ray phase analysis and electric resistance measurements. The compacted powders were annealed in pure Ar atmosphere. It was shown that electrical resistance of the compacted Cu specimens essentially depends on the annealing temperature. In particular, the electrical resistance of the pellet after annealing at 873 K decreases on heating at low temperatures (semiconducting mechanism). As the temperature is increased, semiconducting behavior of resistivity is altered for metallic one. This change of conductivity type is ascribed to formation of metallic oxide and modification of its content during annealing.
منابع مشابه
Spark plasma sintering of alumina nanopowders produced by electrical explosion of wires
Alumina nanopowders produced by electrical explosion of wires were sintered using the spark plasma sintering technique. The results of XRD analysis show that the main phase in the compacted nanopowders is α-Al2O3. According to the SEM observations, the sintered alumina nanopowder consists of micron-sized faceted grains and nano-sized necked grains. The increase in sintering temperature resulted...
متن کاملNanopowder Metal Oxide for Photoluminescent Gas Sensing
Gas sensing properties of metal oxide nanopowders (ZnO, TiO2, WO3, SnO2) with average diameters of 40-60 nm were analyzed by room-temperature photoluminescence spectroscopy. The influence of gas environment (O2, N2, H2, CO, CO2) on the emission intensity was investigated for metal oxide nanopowders with surface doped by impurities (Pt, Ag, Au, Sn, Ni or Cu). Established physicochemical regulari...
متن کاملTHE EFFECT OF COBALT ADDITIVE ON MICROSTRUCTURE AND PROPERTIES OF W-CU COMPOSITES PREPARED BY SINTERING AND INFILTRATION PROCESSES
In the present paper, the influence of cobalt additive on the sintering/infiltration behavior of W-Cu composite was studied. For this purpose, the mixed powders of tungsten and cobalt were compacted by CIP method and then sintered at 1450, 1550 and 1600 °C in a hydrogen atmosphere. The sintered specimens at 1550 °C were subsequently infiltrated with liquid copper at 1250 °C for 10, 60 and 1...
متن کاملInvestigation on Mechanical and Electrical Properties of Cu-Ti Nanocomposite Produced by Mechanical Alloying
In this paper, Cu-Ti nanocomposite synthesized via ball milling of copper-titanium powders in 1, 3, and 6 of weight percentage compounds. The vial speed was 350 rpm and ball to powder weight ratio kept at 15:1 under Argon atmosphere, and the time of milling was 90 h. Obtained powders were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), and dynamic light scattering (DLS)....
متن کاملEffect of Combination on Properties of Cu-Ag Nanocomposites Synthesized by Heat Treatment
Ag-Cu solid solutions prepared via ball milling process were subsequently milled for 30 h and investigated by X-ray diffraction technique for Cu-20%Ag, Cu-3.64%Ag and Cu-80%Ag. It was noted that the solid solubility level increased by increasing initial solute content in composition. Results showed peak positions of silver and copper changed with milling time. By heating up to 700 K, ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره 11 شماره
صفحات -
تاریخ انتشار 2016