Yb 3 + codoped NaMnF 3 nanocubes with single - band red upconversion luminescence †
نویسندگان
چکیده
Wehave developed a facile low-temperature synthetic method for the preparation of NaMnF3 nanocubes with Er 3+ and Yb ions homogeneously incorporated in the host lattice. The effects of the reaction temperature, and the volume ratio between ethanol and DI water on themorphology of NaMnF3 nanocubes are systematically investigated. The NaMnF3 nanocubes can be produced in the low temperature range (25–80 C), and the higher reaction temperature (80 C) is favorable for the formation of a smooth surface. The formation of NaMnF3 nanocubes strongly depends on the ethanol solvent. The morphology and single-phase of the obtained samples could be well maintained by controlling the doping concentration (Yb# 20mol%). Single-band red upconversion emission can be generated in Er/Yb codoped NaMnF3 nanocubes due to the energy transfer between host Mn and dopant Er ions. It is revealed that our NaMnF3:Er /Yb nanocubes irradiate the brightest red luminescence at the dopant concentrations of Er (2 mol%) and Yb (15 mol%), which is stronger than that of the hexagonal-phase NaYF4:Er /Yb phosphor.
منابع مشابه
Color control and white upconversion luminescence of LaOF:Ln3+ (Ln = Yb, Er, Tm) nanocrystals prepared by the sol-gel Pechini method.
A series of Yb(3+)-Er(3+) and Yb(3+)-Er(3+)-Tm(3+) codoped LaOF nanocrystals were synthesized via a modified sol-gel Pechini method. The phases and morphologies as well as the luminescence properties of the as-prepared samples were characterized by means of X-ray diffraction (XRD), scanning electron microscopy (SEM) and upconversion luminescence (UCL) spectra, respectively. Under 980 nm near in...
متن کاملEnhanced upconversion emission in Yb3+ and Er3+ codoped NaGdF4 nanocrystals by introducing Li+ ions.
β-NaGdF(4) : Yb(3+)/Er(3+) nanoparticles (NPs) codoped with Li(+) ions were prepared for the first time via a thermal decomposition reaction of trifluoroacetates in oleylamine. The influence of site occupancy of Li(+) on the upconversion emission of β-NaGdF(4) : Yb(3+)/Er(3+) NPs was investigated in detail. The upconversion emission intensity was significantly enhanced by introducing different ...
متن کاملGreen and red light emission by upconversion from the near-IR in Yb(3+) doped CsMnBr3.
Direct near-IR excitation of Yb(3+) 2F(7/2)-->(2)F(5/2) levels at 10126, 10138, and 10596 cm(-1) in CsMnBr3:0.5%Yb(3+) leads to three types of luminescence at cryogenic temperatures: near-IR Yb(3+) emission and green and red upconverted luminescence. The green luminescence around 20 000 cm(-1) is identified as cooperative Yb(3+) pair upconversion. The broad red upconversion luminescence band ce...
متن کاملMultiple Temperature-Sensing Behavior of Green and Red Upconversion Emissions from Stark Sublevels of Er3+
Upconversion luminescence properties from the emissions of Stark sublevels of Er(3+) were investigated in Er(3+)-Yb(3+)-Mo(6+)-codoped TiO₂ phosphors in this study. According to the energy levels split from Er(3+), green and red emissions from the transitions of four coupled energy levels, ²H11/2(I)/²H11/2(II), ⁴S3/2(I)/⁴S3/2(II), ⁴F9/2(I)/⁴F9/2(II), and ²H11/2(I) + ²H11/2(II)/⁴S3/2(I) + ⁴S3/2(...
متن کاملNaGd(MoO4)2 nanocrystals with diverse morphologies: controlled synthesis, growth mechanism, photoluminescence and thermometric properties
Pure tetragonal phase, uniform and well-crystallized sodium gadolinium molybdate (NaGd(MoO4)2) nanocrystals with diverse morphologies, e.g. nanocylinders, nanocubes and square nanoplates have been selectively synthesized via oleic acid-mediated hydrothermal method. The phase, structure, morphology and composition of the as-synthesized products are studied. Contents of both sodium molybdate and ...
متن کامل