MoS2 Dual-Gate MOSFET With Atomic-Layer-Deposited Al2O3 as Top-Gate Dielectric
نویسندگان
چکیده
We demonstrate atomic-layer-deposited (ALD) high-k dielectric integration on 2-D layer-structured molybdenum disulfide (MoS2) crystals and MoS2 dual-gate n-channel MOSFETs with ALD Al2O3 as the gate dielectric. Our C–V study of MOSFET structures shows good interface between 2-D MoS2 crystal and ALD Al2O3. Maximum drain currents using back gates and top gates are measured to be 7.07 and 6.42 mA/mm, respectively, at Vds = 2 V with a channel width of 3 μm, a channel length of 9 μm, and a top-gate length of 3 μm. We achieve the highest field-effect mobility of electrons using back-gate control to be 517 cm/V · s. The highest current on/off ratio is over 10.
منابع مشابه
Improved Gate Dielectric Deposition and Enhanced Electrical Stability for Single-Layer MoS2 MOSFET with an AlN Interfacial Layer
Transistors based on MoS2 and other TMDs have been widely studied. The dangling-bond free surface of MoS2 has made the deposition of high-quality high-k dielectrics on MoS2 a challenge. The resulted transistors often suffer from the threshold voltage instability induced by the high density traps near MoS2/dielectric interface or inside the gate dielectric, which is detrimental for the practical...
متن کاملAu th or ' s pe rs on al co
We report on a GaN metal-oxide-semiconductor field-effect-transistor (MOSFET) using atomic-layer-deposited (ALD) Al2O3 as the gate dielectric. Compared to a GaN metal-semiconductor field-effect-transistor (MESFET) of similar design, the MOSFET exhibits several orders of magnitude lower gate leakage and near three times higher channel current. This implies that the ALD Al2O3/GaN interface is of ...
متن کاملSubmicrometer inversion-type enhancement-mode InGaAs MOSFET with atomic-layer-deposited Al2O3 as gate dielectric
High-performance inversion-type enhancementmode n-channel In0.53Ga0.47As MOSFETs with atomiclayer-deposited (ALD) Al2O3 as gate dielectric are demonstrated. The ALD process on III–V compound semiconductors enables the formation of high-quality gate oxides and unpinning of Fermi level on compound semiconductors in general. A 0.5-μm gate-length MOSFET with an Al2O3 gate oxide thickness of 8 nm sh...
متن کاملAtomic-layer-deposited Al2O3 on Bi2Te3 for topological insulator field-effect transistors
We report dual-gate modulation of topological insulator field-effect transistors (TI FETs) made on Bi2Te3 thin flakes with integration of atomic-layer-deposited (ALD) Al2O3 high-k dielectric. Atomic force microscopy study shows that ALD Al2O3 is uniformly grown on this layer-structured channel material. Electrical characterization reveals that the right selection of ALD precursors and the relat...
متن کاملProcessing and Characterization of III–V Compound Semiconductor MOSFETs Using Atomic Layer Deposited Gate Dielectrics
We demonstrate III–V compound semiconductor (GaAs, InGaAs, and GaN) based metal-oxide-semiconductor field-effect transistors (MOSFETs) with excellent performance using an Al2O3 high-permittivity (high-k) gate dielectric, deposited by atomic layer deposition (ALD). These MOSFET devices exhibit extremely low gate-leakage current, high transconductance, high dielectric breakdown strength, a high s...