High Temperature Oxidation and Corrosion Properties of High Entropy Superalloys

نویسندگان

  • Te-Kang Tsao
  • An-Chou Yeh
  • Chen-Ming Kuo
  • Hideyuki Murakami
چکیده

The present work investigates the high temperature oxidation and corrosion behaviour of high entropy superalloys (HESA). A high content of various solutes in HESA leads to formation of complex oxides, however the Cr and Al activities of HESA are sufficient to promote protective chromia or alumina formation on the surface. By comparing the oxidation and corrosion resistances of a Ni-based superalloy—CM247LC, Al2O3-forming HESA can possess comparable oxidation resistance at 1100 ̋C, and Cr2O3-forming HESA can exhibit superior resistance against hot corrosion at 900 ̋C. This work has demonstrated the potential of HESA to maintain surface stability in oxidizing and corrosive environments.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Physcial Metallurgy and Microstructure of Superalloys

When significant resistance to loading under static, fatigue and creep conditions is required, the superalloys have emerged as the materials of choice for high temperature applications. This is particularly true when operating temperatures are beyond about 800C. This is the case for gas turbines used for (i) jet propulsion, e.g. the 100,000 lb thrust engines used for powering large two-engined ...

متن کامل

Modeling of the microstructural evolution and lifetime prediction of MCrAlX coatings on Nickel based superalloys in high temperature oxidation

MCrAlY coatings are deposited onto superalloys to provide oxidation and corrosion protection at high temperature by the formation of a thermally grown oxide scale. In this project, the oxidation behaviour of a HVOF CoNiCrAlYSi coating on IN792 was studied for both isothermal oxidation (900, 1000 and 1100 °C) and thermal cycling (100-1100 °C). The microstructural evolution of the CoNiCrAlYSi coa...

متن کامل

The Study of High Temperature Oxidation behavior of Different Microstructures of HVOF Thermally Sprayed Coatings

Improvement of thermally sprayed coating properties by microstructure modification has been considered as a significant solution. Therefore, in this research the effect of dissolved oxygen content and post heat treatment on the formation and distribution of secondary phase particles, particularly in nano-scale in the coatings during spraying and after that were studied. Ni-5 wt% Al powders were...

متن کامل

EFFECT OF HIGH TEMPERATURE OXIDATION ON THE CORROSION BEHAVIOR OF ALUMINIZED LOW CARBON STEEL IN MOLTEN ALUMINUM

Hot dip aluminizing was carried out on the low carbon steel rod under optimized conditions. The aluminized samples were further oxidized at 1000̊C in air atmosphere at two different times of 20 and 60 minutes. Microstructure study and phase analysis were studied by scanning electron microscopy and X-ray diffraction methods, respectively. The characterization of the coating showed that, Fe2...

متن کامل

Metallurgical and mechanical properties of laser cladded AlFeCuCrCoNi-WC10 high entropy alloy coating

In spite of excellent corrosion resistance, good ductility and low cost of AISI 316 austenitic stainless steel, the low hardness and poor mechanical charecteristic of material restricts its applicability in several industrial services. To improve upon mechanical properties AlFeCuCrCoNi-WC10 high-entropy alloy coatings were deposited via laser cladding on austentic stainless steel AISI 316 subst...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Entropy

دوره 18  شماره 

صفحات  -

تاریخ انتشار 2016