Effect of ferrule on the fracture resistance of mandibular premolars with prefabricated posts and cores

PURPOSE This study evaluated fracture resistance with regard to ferrule lengths and post reinforcement on endodontically treated mandibular premolars incorporating a prefabricated post and resin core. MATERIALS AND METHODS One hundred extracted mandibular premolars were randomly divided into 5 groups (n=20): intact teeth (NR); endodontically treated teeth (ETT) without post (NP); ETT restored with a prefabricated post with ferrule lengths of either 0 mm (F0), 1 mm (F1), or 2 mm (F2). Prepared teeth were restored with metal crowns. A thermal cycling test was performed for 1,000 cycles. Loading was applied at an angle of 135 degrees to the axis of the tooth using a universal testing machine with a crosshead speed of 2.54 mm/min. Fracture loads were analyzed by one-way ANOVA and Tukey HSD test using a statistical program (α=.05). RESULTS There were statistical differences in fracture loads among groups (P<.001). The fracture load of F2 (237.7 ± 83.4) was significantly higher than those of NP (155.6 ± 74.3 N), F0 (98.8 ± 43.3 N), and F1 (152.8 ± 78.5 N) (P=.011, P<.001, and P=.008, respectively). CONCLUSION Fracture resistance of ETT depends on the length of the ferrule, as shown by the significantly increased fracture resistance in the 2 mm ferrule group (F2) compared to the groups with shorter ferrule lengths (F0, F1) and without post (NP).