Lamellae Evolution of Stereocomplex-Type Poly(Lactic Acid)/Organically-Modified Layered Zinc Phenylphosphonate Nanocomposites Induced by Isothermal Crystallization
نویسندگان
چکیده
Stereocomplex-type poly(lactic acid) (SC-PLA)/oleylamine-modified layered zinc phenylphosphonate (SC-PLA/m-PPZn) nanocomposites are successfully fabricated using a solution mixing process. Wide-angle X-ray diffraction (WAXD) analysis reveals that the structural arrangement of the oleylamine-modified PPZn exhibits a large interlayer spacing of 30.3 Å. In addition, we investigate the temperature effect on the real-time structural arrangement of PPZn and m-PPZn. The results indicated that the lattice expansion of m-PPZn with increasing temperature leads to an increase in the interlayer spacing from 30.3 to 37.1 Å as the temperature increases from 30 to 150 °C. The interlayer spacing decreases slightly as the temperature further increases to 210 °C. This behavior might be attributed to interlayer oleylamine elimination, which results in hydrogen bonding destruction between the hydroxide sheets and water molecules. As the temperature reaches 240 °C, the in situ WAXD patterns show the coexistence of m-PPZn and PPZn. However, the layered structures of m-PPZn at 300 °C are almost the same as those of PPZn, after the complete degradation temperature of oleylamine. The morphology of the SC-PLA/m-PPZn nanocomposites characterized using WAXD and transmission electron microscopy (TEM) demonstrates that most partial delamination layered materials are randomly dispersed in the SC-PLA matrix. Small-angle X-ray scattering reveals that higher crystal layer thickness and lower surface free energy is achieved in 0.25 wt% SC-PLA/m-PPZn nanocomposites. These results indicate that the introduction of 0.25 wt% m-PPZn into SC-PLA reduces the surface free energy, thereby increasing the polymer chain mobility.
منابع مشابه
Synergistic effects of nucleating agents and plasticizers on the crystallization behavior of poly(lactic acid).
The synergistic effect of nucleating agents and plasticizers on the thermal and mechanical performance of PLA nanocomposites was investigated with the objective of increasing the crystallinity and balancing the stiffness and toughness of PLA mechanical properties. Calcium carbonate, halloysite nanotubes, talc and LAK (sulfates) were compared with each other as heterogeneous nucleating agents. B...
متن کاملMorphological and mechanical properties of Poly (lactic Acid) /zinc oxide nanocomposite films
Objective(s): Nowadays, tendency to use green materials can reduce environmental pollution and plastic waste. Poly (lactic Acid) PLA is one of the natural biodegradable polymers mainly used in the production of bioplastics for packaging which is made of non-toxic compounds and is easily biodegradable. In this research, the effect of 1, 3 and 5% nanocomposite zinc oxide on the morphological, mec...
متن کاملAn investigation on non-isothermal crystallization behavior and morphology of polyamide 6/ poly(ethylene-co-1-butene)-graft-maleic anhydride/organoclay nanocomposites
Nanocomposites based on polyamide 6 (PA6) and poly(ethylene-co-1-butene)-graft-maleic anhydride (EB-g- MAH) blends have been prepared via melt mixing. The effect of blend ratio and organoclay concentration on the crystallization and melting behavior of specimens were studied. Three types of commercial organo-modified clay (Cloisite 30B, Cloisite 15A and Cloisite 20A) were employed to assess the...
متن کاملNon-Isothermal Cold-Crystallization Behavior and Kinetics of Poly(l-Lactic Acid)/WS2 Inorganic Nanotube Nanocomposites
In order to accelerate the crystallization of poly(L-lactic acid) (PLLA) biopolymer and enhance its crystallizability, biocompatible and environmentally friendly tungsten disulphide inorganic nanotubes (INT-WS2) were introduced into the polymer matrix. The non-isothermal cold-crystallization and subsequent melting behaviour of pure PLLA and PLLA/INT-WS2 nanocomposites were investigated in detai...
متن کاملStudy of Non-Isothermal Crystallization Kinetics of Biodegradable Poly(ethylene adipate)/SiO2 Nanocomposites
Poly(ethylene adipte) and poly(ethylene adipate)/silica nanocomposite (PEAd/SiO2) containing 3 wt. % SiO2 were prepared by an in situ method. The examinations on the non-isothermal crystallization kinetic behavior have been conducted by means of differential scanning calorimeter (DSC). The Avrami, Ozawa, and combined Avrami and Ozawa equations were applied to describe the crystallization kinet...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره 9 شماره
صفحات -
تاریخ انتشار 2016