Effect of Film Thickness on the Piezoelectric Properties of Lead Zirconate Titanate Thick Films Fabricated by Aerosol Deposition
نویسندگان
چکیده
Lead zirconate titanate (PZT) thick films with uniformly dispersed submicrometer pores were successfully fabricated on platinized silicon substrates with various thicknesses ranging from 1 lm to over 100 lm by aerosol deposition. Mixed powders of PZT and polyvinylidene fluoride (PVDF) were deposited for initial fabrication of composite films. After burn-out of the PVDF phase from the composite films during postannealing processing at 7001C, uniformly dispersed submicrometer pores capable of relaxing the residual stress were generated in the PZT thick films. The dielectric and piezoelectric properties were improved with increasing film thickness due to the minimization of the interfacial clamping effect.
منابع مشابه
Effects of thickness on the piezoelectric and dielectric properties of lead zirconate titanate thin films
Lead zirconate titanate ~PZT! thin films with a Zr/Ti ratio of 52/48 were deposited on platinized silicon substrates by a sol-gel method and crystallized with preferred ~111! or ~100! orientation. Both the piezoelectric properties (d33) and the field-induced strains of the films with different thickness and preferred orientation were measured by a laser Doppler heterodyne interferometer. The we...
متن کاملThickness dependence of structural and electrical properties in epitaxial lead zirconate titanate films
We have studied the effect of misfit strain on the microstructure and properties of ferroelectric lead zirconate titanate thin films. We have changed the misfit strain by varying the film thickness and studied the thickness effect on the domain formation of epitaxial PbZr0.2Ti0.8O3 ~PZT! films grown by pulsed laser deposition on ~001! LaAlO3 substrates with La0.5Sr0.5CoO3 ~LSCO! electrodes. The...
متن کاملStrongly Enhanced Piezoelectric Response in Lead Zirconate Titanate Films with Vertically Aligned Columnar Grains
Pb(Zr0.52Ti0.48)O3 (PZT) films with (001) orientation were deposited on Pt(111)/Ti/SiO2/Si(100) substrates using pulsed laser deposition. Variation of the laser pulse rate during the deposition of the PZT films was found to play a key role in the control of the microstructure and to change strongly the piezoelectric response of the thin film. The film deposited at low pulse rate has a denser co...
متن کاملMicrostereolithography of lead zirconate titanate thick film on silicon substrate
Ž . Ž . The microstereolithography mSL of lead zirconate titanate PZT thick films on platinum-buffered silicon substrates is reported for Ž . the first time in this paper. Crack-free PZT thick films 80–130 mm thick have been fabricated by laser direct-write UV polymerization from the HDDA-based UV curable PZT suspensions. The characterization of the fired films shows dielectric permittivities o...
متن کاملInfluence of PZT Coating Thickness and Electrical Pole Alignment on Microresonator Properties
With increasing technical requirements in the design of microresonators, the development of new techniques for lightweight, simple, and inexpensive components becomes relevant. Lead zirconate titanate (PZT) is a powerful tool in the formation of these components, allowing a self-actuation or self-sensing capability. Different fabrication methods lead to the variation of the properties of the de...
متن کامل