Electrostatic capacitance of TiO2 nanowires in a porous alumina template

نویسندگان

  • Jaeyoung Lee
  • Jinsub Choi
  • Jaekwang Lee
  • Sang Kyo Choi
  • Hee Dong Chun
چکیده

Titanium oxide (TiO2) nanowires were prepared for an electrolytic capacitor application by the automatic dipping technique using a porous alumina template. The automatic dipping technique allows us to exactly control the dipping rate so that we can obtain homogenous infiltration of nanowires in the porous alumina membrane, even though the solution is very acidic. From the TEM, SEM and XRD measurements, we confirmed that anatase phase TiO2 nanowires are highly infiltrated into the porous alumina template. In addition, the electrostatic capacitance of nanowires was measured and compared with a theoretical calculation using an effective thickness (δe). We found that the effective thickness corresponds to the mean radius of nanowires and the experimental measurements were in good agreement with the calculations.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

The effect of pulsed electrodeposition parameters on the microstructure and magnetic properties of the CoNi nanowires

CoNi nanowires were deposited by pulsed electrodeposition technique into porous alumina templates. The effect of off time between pulses (toff) and reductive/oxidative time (treduc/oxid) on the microstructure and magnetic properties of the CoNi nanowires were investigated. Maximum coercivity and squareness were obtained for samples fabricated at treduc/oxid= 0.5 ms and toff =400 ms. The coerciv...

متن کامل

Highly organised and dense vertical silicon nanowire arrays grown in porous alumina template on <100> silicon wafers

In this work, nanoimprint lithography combined with standard anodization etching is used to make perfectly organised triangular arrays of vertical cylindrical alumina nanopores onto standard <100>-oriented silicon wafers. Both the pore diameter and the period of alumina porous array are well controlled and can be tuned: the periods vary from 80 to 460 nm, and the diameters vary from 15 nm to an...

متن کامل

Cu(2)O nanowires in an alumina template: electrochemical conditions for the synthesis and photoluminescence characteristics.

Cu2O nanowires, mainly consisting of (100) and (200) polycrystalline structures with a length of 4 mum are prepared by electrochemical deposition using a porous alumina template. It is found that the optimized electrochemical conditions to prepare Cu2O nanowires are different from those for the formation of a bulk thin Cu2O layer since different pH values are found between the tip of the pores ...

متن کامل

Properties of Ni and Ni–Fe nanowires electrochemically deposited into a porous alumina template

The comparative analysis of the electrochemical deposition of Ni and Ni-Fe nanowires (NWs) into ordered porous alumina templates is presented. The method developed allows for obtaining NWs of 50 ± 5 nm in diameter and 25 μm in length, i.e., with an aspect ratio of 500. XRD data demonstrate the polycrystalline nature of Ni and Ni-Fe in a face-centered cubic close-packed lattice. Both fabricated ...

متن کامل

Liquid crystalline nanowires in porous alumina: geometric confinement versus influence of pore walls.

Aligned liquid crystalline nanowires within ordered porous alumina templates show a pronounced texture on a macroscopic scale. We have investigated the influence of the geometric confinement and the nature of the pore walls on the mesophase formation by means of X-ray diffraction. The apparent texture is the result of a complex interplay of the pore geometry, interfacial phenomena, and the ther...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2005