Change in thermal transitions and water uptakes of poly(l-lactic acid) blends upon hydrolytic degradation
نویسندگان
چکیده
This article reports experimental data related to the research article entitled "Poly(malic acid-co-l-lactide) as a Superb Degradation Accelerator for Poly(l-lactic acid) at Physiological Conditions" (H.T. Oyama, D. Tanishima, S. Maekawa, 2016) [1]. Hydrolytic degradation of poly(l-lactic acid) (PLLA) blends with poly(aspartic acid-co-l-lactide) (PAL) and poly(malic acid-co-l-lactide) (PML) oligomers was investigated in a phosphate buffer solution at 40 °C. It was found in the differential scanning calorimetry measurements that upon hydrolysis the cold crystallization temperature (Tc ) and the melting temperature (Tm ) significantly shifted to lower temperature. Furthermore, the hydrolysis significantly promoted water sorption in both blends.
منابع مشابه
Degradability of cross-linked polyurethanes based on synthetic polyhydroxybutyrate and modified with polylactide
In many areas of application of conventional non-degradable cross-linked polyurethanes (PUR), there is a need for their degradation under the influence of specific environmental factors. It is practiced by incorporation of sensitive to degradation compounds (usually of natural origin) into the polyurethane structure, or by mixing them with polyurethanes. Cross-linked polyurethanes (with 10 and ...
متن کاملEffects of poly(L-lactide-ε-caprolactone) and magnesium hydroxide additives on physico-mechanical properties and degradation of poly(L-lactic acid)
BACKGROUND Biodegradable poly(L-lactic acid) (PLLA) is one of the most widely used polymer in biomedical devices, but it still has limitations such as inherent brittleness and acidic degradation products. In this work, PLLA blends with poly(L-lactide-ε-caprolactone) (PLCL) and Mg(OH)2 were prepared by the thermal processing to improve their physico-mechanical and thermal properties. In addition...
متن کاملThermo-mechanical properties of poly ε-caprolactone/poly L-lactic acid blends: addition of nalidixic acid and polyethylene glycol additives.
The search for ideal biomaterials is still on-going for tissue regeneration. In this study, blends of poly ε-caprolactone (PCL) with poly l-lactic acid (PLLA), nalidixic acid (NA) and polyethylene glycol (PEG) were prepared. Mechanical and thermal properties of the blends were investigated by tensile and flexural analysis, DSC, TGA, WXRD, MFI, BET, SEM and hot stage optical microscopy. Results ...
متن کاملWater absorption and degradation characteristics of chitosan-based polyesters and hydroxyapatite composites.
Blends of chitosan and biodegradable synthetic aliphatic polyesters (polycaprolactone, poly(butylene succinate), poly[(butylene succinate)-co-adipate], poly[(butylene terephthalate)-co-adipate], and poly(lactic acid)) were injection-molded. These samples were immersed in isotonic solution at 37 degrees C for a period of 60 d. The water uptake and the degradation properties, as measured by the l...
متن کاملInvestigation into the effect of UV/Ozone Irradiation on the dyeing behaviour of Poly(lactic acid) and Poly(ethylene terephthalate) Substrates
The effect of UV/Ozone irradiation together with the pretreatments using distilled water, hydrogen peroxide, and hydrogen peroxide/sodium silicate solutions on the dyeing depth of the poly(lactic acid), PLA, and poly(ethylene terephthalate), PET, fabrics by the application of disperse dyes were investigated and the results were compared with that of untreated fabrics. The results showed that th...