Ceramic bonding strength of Au-1.6 wt% Ti alloy.
نویسندگان
چکیده
The aim of this investigation was to evaluate the metal-ceramic bonding of Au-1.6 wt% Ti alloy. Therefore, the coefficient of thermal expansion, modulus of elasticity, ceramic bonding strength, and hardness of Au-1.6 wt% Ti alloy were measured. The metal-ceramic interface was observed by EPMA to investigate its bonding mechanism. The Au-1.6 wt% Ti alloy showed a coefficient of thermal expansion close to that of conventional precious metal alloys for metal-ceramics. Bonding strength was 25 MPa or higher for all specimens--whether ceramic-fired directly after casting, or following oxidation treatment or age hardening. Specimens subjected to oxidation treatment showed slightly lower post-firing hardness than those age-hardened. EPMA observation showed an accumulation of Ti and O contents on the alloy side at the metal-ceramic interface.
منابع مشابه
Effect of metal primers and tarnish treatment on bonding between dental alloys and veneer resin
PURPOSE The aim of this study was to evaluate the effect of metal primers on the bonding of dental alloys and veneer resin. Polyvinylpyrrolidone solution's tarnish effect on bonding strength was also investigated. MATERIALS AND METHODS Disk-shape metal specimens (diameter 8 mm, thickness 1.5 mm) were made from 3 kinds of alloy (Co-Cr, Ti and Au-Ag-Pd alloy) and divided into 4 groups per each ...
متن کاملEffect of alumina air-abrasion on mechanical bonding between an acrylic resin and casting alloys.
This study examined the effect of alumina air-abrasion with different pressure on bonding between an acrylic resin and casting alloys. Disk specimens (8 and 10 mm in diameter) were cast from a silver-palladium-copper-gold (Ag-Pd-Cu-Au, Castwell M.C.12) alloy and a titanium-aluminum-niobium alloy (Ti-6Al-7Nb, T-Alloy Tough). The disks were air-abraded with alumina particles (50-70 microm) under ...
متن کاملWear studies on plasma-sprayed Al2O3 and 8mole% of Yttrium-stabilized ZrO2 composite coating on biomedical Ti-6Al-4V alloy for orthopedic joint application
This paper presents the wear characteristics of the composite ceramic coating made with Al2O3-40wt%8YSZ on the biomedical grade Ti-6Al-4V alloy (grade 5) used for total joint prosthetic components, with the aim of improving their tribological behavior. The coatings were deposited using a plasma spraying technique, and optimization of plasma parameters was performed using response surface method...
متن کاملMicrostructure and Grain Refining Performance of a New Al-Ti-C Master Alloy (RESEARCH NOTE)
Control of microstructure parameters that affecting the Al-Ti-C master alloys grain refining efficiency is leading to improve the aluminum grain refinement. This study was an attempt to produce Al-Ti-C master alloys that provide these controlling factors with relying on the solute effect theory. The produced master alloys were examined by using scanning electron microscopy (SEM), energy-dispers...
متن کاملBonding properties of heat-polymerized denture base resin to Ti-6Al-7Nb alloy.
The purpose of this study was to evaluate the shear bonding strength and leakage of heat-polymerized denture base resin to titanium-aluminum-niobium (Ti-6Al-7Nb) and cobalt-chromium (Co-Cr) castings using four adhesive systems; three adhesive primers (Metal Primer II, Metal Link, MR. Bond) and one heat-polymerized adhesive resin containing 4-META (Metadent). The resin tab was heat-polymerized d...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Dental materials journal
دوره 24 2 شماره
صفحات -
تاریخ انتشار 2005